DALI ELECTRONICS 8/A, Haroon Building, 190 Shamaldas Gandhi Marg, Mumbai 400002, India MµMetal / MuMetal / µMetal / HyMu80 / / 80 / Super Muniperm / FeNi80Mo5 / Super MuMetal / SofMag80 / Supermalloy / Aperam / Permimphy / Permalloy C / EFI 79 / Magnifer 7904 / Hipernom / Moly-Permalloy / Amumetal

International standards: ASTM A 753, DIN 17405, IEC 404, JIS C 2531 Chemical Composition: Nickel 80%, Molybdenum 5%, Iron Balance, Some impurities

Physical Properties Metric English Density 8.74 g/cc 0.316 lb/in³

Mechanical Properties Metric English Hardness, Brinell 105 - 290 105 - 290 Tensile Strength at Break 530 - 900 MPa 76900 - 131000 psi Tensile Modulus 190 - 221 GPa 27600 - 32100 ksi Izod Impact, Unnotched 0.420 - 1.00 J/cm 0.787 - 1.87 ft-lb/in

Electrical Properties Metric English Electrical Resistivity 0.0000550 - 0.0000620 ohm-cm 0.0000550 - 0.0000620 ohm-cm Magnetic Permeability min 60000 min 60000 max 240000 max 240000 Magnetic Coercive Force, Hc 0.0126 Oe 0.0126 Oe Magnetic , Br 3700 Gauss 3700 Gauss 380 °C 716 °F

Thermal Properties Metric English CTE, linear 13.0 µm/m-°C 7.22 µin/in-°F @Temperature 20.0 - 100 °C @Temperature 68.0 - 212 °F Thermal Conductivity 30.0 - 35.0 W/m-K 208 - 243 BTU-in/hr-ft²-°F

Component Elements Properties Metric English Iron, Fe 14 % 14 % Molybdenum, Mo 4-6 % 4-6 % Nickel, Ni 79-81 % 79-81 %

Descriptive Properties Induction (T) 0.77

www.DOMADIA.com www.DOMADIA.net +91-9821236275 / 9594066275 DALI ELECTRONICS 8/A, Haroon Building, 190 Shamaldas Gandhi Marg, Mumbai 400002, India

Mu-metal is a nickel–iron soft magnetic alloy with very high permeability, which is used for shielding sensitive electronic equipment against static or low-frequency magnetic fields.

Mu-metal typically has relative permeability values of 80,000–100,000 compared to several thousand for ordinary steel. It is a "soft" magnetic material; it has low and , giving it a low so that it saturates at low magnetic fields. This gives it low losses when used in AC magnetic circuits. mu-metal has more advantage as it is more ductile and workable, allowing it to be easily formed into the thin sheets needed for magnetic shields.

Mu-metal objects require heat treatment after they are in final form—annealing in a in atmosphere, which increases the magnetic permeability about 40 times. The annealing alters the material's crystal structure, aligning the grains and removing some impurities, especially , which obstruct the free motion of the boundaries. Bending or mechanical shock after annealing may disrupt the material's grain alignment, leading to a drop in the permeability of the affected areas, which can be restored by repeating the hydrogen annealing step.

Magnetic shielding The high permeability of mu-metal provides a low reluctance path for magnetic flux, leading to its use in magnetic shields against static or slowly varying magnetic fields. Magnetic shielding made with high- permeability alloys like mu-metal works not by blocking magnetic fields but by providing a path for the magnetic field lines around the shielded area. Thus, the best shape for shields is a closed container surrounding the shielded space. The effectiveness of mu-metal shielding decreases with the alloy's permeability, which drops off at both low field strengths and, due to saturation, at high field strengths. Thus, mu-metal shields are often made of several enclosures one inside the other, each of which successively reduces the field inside it. Because mu-metal saturates at such low fields, sometimes the outer layer in such multilayer shields is made of ordinary steel. Its higher saturation value allows it to handle stronger magnetic fields, reducing them to a lower level that can be shielded effectively by the inner mu-metal layers.

Popular Shielding Applications of MuMetal  Shielding of RF magnetic fields  cryogenic Shields  Shielding from natural Earth  cathode ray tubes (CRTs) used in oscilloscopes  sensitive electronic equipment against magnetic field  AC magnetic circuits  shield against  Mobile Networks & Antennas Rays  Shielding of SQUID – Superconducting Quantum Interference Device -  telegraph cables  Electric power , which are built with mu-metal shells to prevent them from affecting nearby circuitry. high quality but low noise audio frequency transformers.  Hard disks, which have mu-metal backings to the magnets found in the drive to keep the magnetic field away from the disk  Cathode-ray tubes used in analogue oscilloscopes, which have mu-metal shields to prevent stray magnetic fields from deflecting the electron beam  Magnetic phonograph cartridges, which have a mu-metal case to reduce interference when LPs are played back  Magnetic resonance imaging equipment www.DOMADIA.com www.DOMADIA.net +91-9821236275 / 9594066275 DALI ELECTRONICS 8/A, Haroon Building, 190 Shamaldas Gandhi Marg, Mumbai 400002, India

 The used in magnetoencephalography and magnetocardiography  Photomultiplier tubes  Vacuum chambers for experiments with low-energy electrons, for example, photoelectron spectroscopy.  Superconducting circuits and especially Josephson junction circuits  Fluxgate magnetometers and compasses as part of the  ground fault interrupter cores  anti-shoplifting devices  tape recorder head laminations  bobbin cores

Frequently Asked Questions (FAQ)

What is a magnetic field? We are surrounded by magnetic fields (both AC and DC) from the earth’s magnetic field to man-made sources such as magnets, motors and transformers. When a piece of sensitive equipment is being affected by these fields we need to produce a shield. Examples that are affected are cathode ray tubes, photomultiplier tubes, audio transformers, scanning electron microscopes, position .

How does a magnetic shield work? There is no known material that can block magnetic fields without itself being attracted to the magnetic force. A magnetic shield acts as a kind of sponge redirecting the magnetic field around the shield instead of passing through the sensitive instrument which is being shielded. To be a good magnetic shielding material it must have a high permeability which means that the magnetic field lines are strongly attracted to the shielding material.

The most common shielding alloys are chosen based on the intensity of the magnetic field. If the magnetic field is too high for the material chosen it will saturate and become ineffective. In this case you can use a multi layer shield with a combination of the different alloys. Alloys should also have a very low remanence to prevent them becoming permanently magnetised.

What is the best shape for a shield? The most efficient shape is spherical but this is very difficult to produce and largely impractical in most shielding applications. The next best is a cylinder with closed ends. These end caps significantly increase the shielding attenuation. This is followed by a box shape but the corners need to have a large bend radius to minimise flux leakage. If possible do not use a flat sheet .

What is the difference between RF and Magnetic Shielding? Radio Frequency shielding is required to stop high frequency fields (> 100 kHz) and copper, , metallised plastics are normally used because they are conductive and have very little permeability. Magnetic shielding is typically found in the 30 – 300 Hz AC range.

What is the difference between DC and AC? DC is direct current that flows in one direction only such as the fields emitted from the Earth or produced by magnets and some motors. AC is alternating current that reverses its direction over a short period and these fields are generated by typical 50-60 Hz electric power equipment. Magnetic shielding is effective for both of these types.

What is magnetic permeability? It is a materials ability to absorb magnetic flux. It is a ratio of flux density to field strength. The higher the permeability the better the magnetic shield attenuation performance. www.DOMADIA.com www.DOMADIA.net +91-9821236275 / 9594066275 DALI ELECTRONICS 8/A, Haroon Building, 190 Shamaldas Gandhi Marg, Mumbai 400002, India

What is field attenuation? This is also known as the shielding factor (S) and is a ratio of the magnetic field strength outside of the magnetic shield (Ha) and the resultant field on the inside of the shield ie Ha/Hi (no units) or S = 20 x log(Ha/Hi) (Db). There are various formula based on the permeability of the material, the shape and size of the shield and the material thickness. In most cases these formulae are only approximate and are for DC fields only.

For a closed shielding can : S = 4/3 X (Mu x d/D) where Mu : The permeability(relative) d : material thickness D : Shielding Diameter

For a long hollow cylinder in a magnetic transverse field : S = Mu x d/D For a cubic shielding box : S = 4/5 X (Mu x d/a) a : box side length.

In the case of multiple layer shields with air gaps provided by insulating spacers the shielding factors of the individual shields are multiplied together resulting in excellent shielding factors.

For a double layer shield : S= S1 x ((S2 x (2 x change in diameter /diameter) )

Why are both, FeNi48 and MuMetal used together? It is has got a very high level of permeability but a relatively low level of saturation whereas , FeNi48 has a lower level of permeability but a level of higher saturation. FeNi48 is used closest to the very strong field to protect the material according to Mumetal from saturation.

Why is a final heat treatment required for Mµ-Metal, FeNi48 and pure iron? After plastic deformation a high temperature heat treatment is required to rearrange the crystal structure as well as allowing the grains to grow. Without this final heat treatment the magnetic properties and the shielding attenuation will be much reduced.

Do cryogenic temperatures affect the performance of MuMetal? MuMetal is affected by cryogenic temperatures. The saturation induction remains the same but the permeability decreases. At cryogenic temperatures we need to use a special cryogenic MuMetall, which we also supply.

Can you use magnetic shielding materials at high vacuum? MuMetal is similar to stainless steel so out gassing is minimal.

Can a shield be re heat treated? Yes it can be if it has received knocks or if there are concerns about the shields shielding ability.

Do you carry stocks of shielding alloys? Yes. We carry and sell a large range of stock including sheets and coil from 0.1mm to 5mm in thickness in MuMetal quality.

Can you weld material µ-Metal? Yes without a problem but it must be fully heat treated after welding.

What is the Minimum Order Quantity required to buy? If we have material in stock, there is no MOQ. We can give minimum of 300 mm / 1 feet too. But if we do not have stock, it will depend on the size and quantity. www.DOMADIA.com www.DOMADIA.net +91-9821236275 / 9594066275 DALI ELECTRONICS 8/A, Haroon Building, 190 Shamaldas Gandhi Marg, Mumbai 400002, India

What are the sizes Available? We have the following stock of the FOILS available with us. Please confirm the length required, so that we can send a quote: 0.025 mm x 100 mm - 1 kg (Auerhammer Metallwerk Gmbh, Germany) 0.03 x 60 x 1500 mm (Auerhammer Metallwerk Gmbh, Germany) 0.05 mm x 100 mm - 4 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.0508 mm x 304 x 3048 mm (USA) 0.1 mm x 304 x 3048 mm (USA) 0.13 X 108 mm - 43 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.2 x 310mm = 96 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.2 x 340 mm – 300 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.25 x 340 mm – 344 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.25 x 152mm - 93.5 kgs 0.5 x 231 mm – 168 kgs (Auerhammer Metallwerk Gmbh, Germany) 0.5 x 30 mm – 0.42 kg (Auerhammer Metallwerk Gmbh, Germany) 0.8 x 113mm – 9.88 kgs

With Best Regards, Kairav Pankaj Domadia +91-9594066275

DALI ELECTRONICS 8/a, Haroon Building, 1st Floor, 190 Shamaldas Gandhi Marg, Mumbai 400002, India Ph +91.22.22017128; +91.22.22038204 www.DOMADIA.net