Material Properties Possible Applications Range [° C] Pt 1769 High Thermal and Chemical Laboratory Apparatus Such As Stability

Total Page:16

File Type:pdf, Size:1020Kb

Material Properties Possible Applications Range [° C] Pt 1769 High Thermal and Chemical Laboratory Apparatus Such As Stability Melting Material point or Material properties Possible applications range [° C] Pt 1769 High thermal and chemical Laboratory apparatus such as stability. Platinum in various crucibles and dishes which are purities. only exposed to low mechanical stresses. Pt-DPH 1769 The finely dispersed oxide Laboratory equipment and particles in platinum and platinum structural components which are PtAu 95/5-DPH 1675 - 1745 alloys significantly increase the subject to high mechanical mechanical strength and stresses at high temperatures. PtRh 90/10-DPH 1840 - 1870 corrosion resistance. PtIr 97/3 1772 - 1773 The mechanical strength, thermal Laboratory apparatus or structural and corrosion resistance become components which are exposed PtIr 90/10 1780 - 1800 greater with increasing iridium to severe mechanical, thermal content. Platinum Iridium alloys and corrosive effects. PtIr 80/20 1830 - 1855 suffer from increased weight loss in oxidizing atmosphere. PtRh 90/10 1840 - 1870 The mechanical strength, thermal Heavy duty laboratory equipment, and corrosion resistance become electrodes, glass fibre bushings PtRh 80/20 1870 - 1910 greater with increasing rhodium and lining materials for content. An advantage of the components to contain molten platinum-rhodium alloys is that glass. only a minimal weight loss occurs even in oxidizing atmosphere. Platilab 11 Small quantities of platinum group Laboratory apparatures or metals have been added to high structural components which are purity platinum, in order to obtain exposed to severe mechanical, a finer crystal structure for better thermal and corrosive effects. chemical and mechanical characteristics. PtAu 95/5 1675 - 1745 The gold content reduces the These properties predestine PtAu wetting by glass melts so that the 95/5 as the material for apparatus glass can be easily removed after for the preparation of samples for solidification without leaving any X-ray fluorescence analysis residues. The mechanical (XRF). strength is also increased and the tendency to recrystallization reduced. Seite 2 AuPt 90/10 1120 - 1180 This gold alloy shows increased Dishes, e.g. for flour ignition, mechanical strength compared sugar ignition, etc. with pure gold and good resistance to phosphorus. Platinum based alloys are more susceptible to corrosion by phosphorus. Ag 961 Good conductivity, chemical Crucibles for reagents which stability (in particular, resistant to corrode platinum alloys; contact Au 1063 phosphorus). materials. Ir 2447 Iridium is the preferred material Crucibles for crystal growing. for oxide melts because of its Components which are subject to good corrosion resistance and severe thermal conditions. high temperature stability in inert atmospheres. The alloys listed in the table above represent only a small selection of the alloys produced by Heraeus. We are pleased to help you with your inquiries or special requirements. .
Recommended publications
  • Package 'Ciaawconsensus'
    Package ‘CIAAWconsensus’ September 19, 2018 Type Package Title Isotope Ratio Meta-Analysis Version 1.3 Author Juris Meija and Antonio Possolo Maintainer Juris Meija <[email protected]> Description Calculation of consensus values for atomic weights, isotope amount ratios, and iso- topic abundances with the associated uncertainties using multivariate meta-regression ap- proach for consensus building. License Unlimited LazyData yes Imports mvtnorm, stringr, numDeriv, stats, Matrix NeedsCompilation no Repository CRAN Date/Publication 2018-09-19 13:30:12 UTC R topics documented: abundances2ratios . .2 at.weight . .3 ciaaw.mass.2003 . .4 ciaaw.mass.2012 . .5 ciaaw.mass.2016 . .6 iridium.data . .6 mmm ............................................7 normalize.ratios . .8 platinum.data . .9 Index 10 1 2 abundances2ratios abundances2ratios Isotope ratios of a chemical element from isotopic abundances Description This function calculates the isotope ratios of a chemical element from the given isotopic abundances and their uncertainties. The uncertainty evaluation is done using the propagation of uncertainty and the missing correlations between the isotopic abundances are reconstructed using Monte Carlo methods. Usage abundances2ratios(x, ux, ref=1, iterations=1e4) Arguments x A vector of isotopic abundances of an element ux Standard uncertainties of x ref Index to specify the desired reference isotope for isotope amount ratios iterations Number of iterations for isotopic abundance correlation mapping Details Situations are often encountered where isotopic abundances are reported but not the isotope ratios. In such cases we reconstruct the isotope ratios that are consistent with the abundances and their uncertainties. Given only the abundances and their uncertainties, for elements with four or more isotopes one cannot unambiguously infer the uncertainties of the ratios due to the unknown correla- tions between isotopic abundances.
    [Show full text]
  • Iridium Platinum Alloys
    Iridium Platinum Alloys A CRITICAL REVIEW OF THEIR CONSTITUTION AND PROPERTIES By A. s. Darling, Ph.D., A.M.1.Mech.E. Native crystals of iridium-platinum are Journal of Science, in 1860, remarked some- frequently found in association with platinum what incredulously: “The platinum makers of ores. These natural alloys, of rather variable Paris are manufacturing these alloys and composition, occur as grains, and sometimes contrary to the wishes of the discoverers are as small cubes with rounded edges. Although extracting higher prices for them than for the geographical distribution is fairly wide pure platinum”. the major deposits appear to be in the Urals. Prominent physicists were, at this period One such crystal, described in I940 by Masing, of the nineteenth century, devoting consider- Eckhardt and Kloiber (I) had a well-defined able effort to the problems involved in repre- two-phase micro-structure. senting their fundamental and derived units Synthetic alloys were produced at an early in concrete form. Iridium-platinum alloys date. Gaudin (z), who fused spheres of a came to fill a unique position in the scale 10per cent iridium-platinum alloy on hearths of substances capable of retaining indefin- of lime and magnesia, commented in 1838 itely their mass, form, and linear dimensions. upon the lustre, malleability and extreme In addition to their corrosion resistance corrosion resistance of the resultant product. and good mechanical properties they were Twenty years later, however, iridium was readily workable and of fairly high electrical still regarded as a troublesome impurity in resistance. No internal transformations were platinum, but the researches of Sainte-Claire recognised in those days and the alloys were Deville and Debray (3) did much to dispel established as materials par exceZZence for this illusion.
    [Show full text]
  • The Development of the Periodic Table and Its Consequences Citation: J
    Firenze University Press www.fupress.com/substantia The Development of the Periodic Table and its Consequences Citation: J. Emsley (2019) The Devel- opment of the Periodic Table and its Consequences. Substantia 3(2) Suppl. 5: 15-27. doi: 10.13128/Substantia-297 John Emsley Copyright: © 2019 J. Emsley. This is Alameda Lodge, 23a Alameda Road, Ampthill, MK45 2LA, UK an open access, peer-reviewed article E-mail: [email protected] published by Firenze University Press (http://www.fupress.com/substantia) and distributed under the terms of the Abstract. Chemistry is fortunate among the sciences in having an icon that is instant- Creative Commons Attribution License, ly recognisable around the world: the periodic table. The United Nations has deemed which permits unrestricted use, distri- 2019 to be the International Year of the Periodic Table, in commemoration of the 150th bution, and reproduction in any medi- anniversary of the first paper in which it appeared. That had been written by a Russian um, provided the original author and chemist, Dmitri Mendeleev, and was published in May 1869. Since then, there have source are credited. been many versions of the table, but one format has come to be the most widely used Data Availability Statement: All rel- and is to be seen everywhere. The route to this preferred form of the table makes an evant data are within the paper and its interesting story. Supporting Information files. Keywords. Periodic table, Mendeleev, Newlands, Deming, Seaborg. Competing Interests: The Author(s) declare(s) no conflict of interest. INTRODUCTION There are hundreds of periodic tables but the one that is widely repro- duced has the approval of the International Union of Pure and Applied Chemistry (IUPAC) and is shown in Fig.1.
    [Show full text]
  • The Separation and Determination of Osmium and Ruthenium
    Louisiana State University LSU Digital Commons LSU Historical Dissertations and Theses Graduate School 1969 The epS aration and Determination of Osmium and Ruthenium. Harry Edward Moseley Louisiana State University and Agricultural & Mechanical College Follow this and additional works at: https://digitalcommons.lsu.edu/gradschool_disstheses Recommended Citation Moseley, Harry Edward, "The eS paration and Determination of Osmium and Ruthenium." (1969). LSU Historical Dissertations and Theses. 1559. https://digitalcommons.lsu.edu/gradschool_disstheses/1559 This Dissertation is brought to you for free and open access by the Graduate School at LSU Digital Commons. It has been accepted for inclusion in LSU Historical Dissertations and Theses by an authorized administrator of LSU Digital Commons. For more information, please contact [email protected]. ThU dissertation has been 69-17,123 microfilmsd exactly as received MOSELEY, Harry Edward, 1929- THE SEPARATION AND DETERMINATION OF OSMIUM AND RUTHENIUM. Louisiana State University and Agricultural and Mechanical College, PhJ>., 1969 Chemistry, analytical University Microfilms, Inc., Ann Arbor, Michigan THE SEPARATION AND DETERMINATION OF OSMIUM AND RUTHENIUM A Dissertation Submitted to the Graduate Faculty of the Louisiana State University and Agricultural and Mechanical College in partial fulfillment of the requirements for the degree of Doctor of Philosophy in The Department of Chemistry Harry Edward Moseley B.S., Lpuisiana State University, 1951 M.S., Louisiana State University, 1952 J anuary, 1969 ACKNOWLEDGMENTS Thanks are due to Dr. Eugene W. Berg under whose direction this work was performed, to Dr. A. D. Shendrikar for his help in the tracer studies, and to Mr. J. H. R. Streiffer for his help in writing the com­ puter program.
    [Show full text]
  • A History of Iridium OVERCOMING the DIFFICULTIES of MELTING and FABRICATION by L
    A History of Iridium OVERCOMING THE DIFFICULTIES OF MELTING AND FABRICATION By L. B. Hunt The Johnson Matthey Group The use in unmanned space craft of iridium to encapsulate the radio- isotope thermoelectric generators, where temperatures of up to 20OO0C have to be withstood over several years of operation, with possible impact velocities of 90 metres per second, has focused greater attention on the remarkable properties of this member of the platinum group of metals. But these same properties of very high melting point and great mechanical strength have been the cause of difficulties in its melting and fabrication over a long period of years. How these problems were tackled and eventually overcome is described in this article. One of the less well-known members of the For some fifty years after the discovery of platinum group, iridium possesses quite platinum in South America and the early remarkable chemical and physical properties. It investigations of its properties by a number of is not only the most resistant of all metals to English, French, German and Swedish scien- corrosion, insoluble in all mineral acids in- tists, it was not realised that the native platinum cluding aqua regia and unattacked by other they were examining also contained other molten metals or by silicates at high tem- elements. The first to recognise that a small in- peratures, but has a very high melting point soluble residue survived the dissolution of and is the only metal to maintain good native platinum in aqua regia was the French mechanical properties in air at temperatures chemist Joseph Louis Proust, working for a above 1600OC.Its great stability can be gauged time in Madrid under the patronage of King from its physical properties, outlined in the Carlos IV, but he failed to grasp that other Table.
    [Show full text]
  • P–V–T Equation of State of Iridium up to 80 Gpa and 3100 K
    crystals Article P–V–T Equation of State of Iridium Up to 80 GPa and 3100 K Simone Anzellini 1,* , Leonid Burakovsky 2, Robin Turnbull 3 , Enrico Bandiello 3 and Daniel Errandonea 3 1 Diamond Light Source Ltd., Harwell Science & Innovation Campus, Diamond House, Didcot OX11 0DE, UK 2 Los Alamos National Laboratory, Theoretical Divisions, Los Alamos, NM 87545, USA; [email protected] 3 Departamento de Física Aplicada-Instituto de Ciencia de Materiales, Matter at High Pressure (MALTA) Consolider Team, Universidad de Valencia, Edificio de Investigación, C/Dr. Moliner 50, Burjassot, 46100 Valencia, Spain; [email protected] (R.T.); [email protected] (E.B.); [email protected] (D.E.) * Correspondence: [email protected] Abstract: In the present study, the high-pressure high-temperature equation of the state of iridium has been determined through a combination of in situ synchrotron X-ray diffraction experiments using laser-heating diamond-anvil cells (up to 48 GPa and 3100 K) and density-functional theory calcula- tions (up to 80 GPa and 3000 K). The melting temperature of iridium at 40 GPa was also determined experimentally as being 4260 (200) K. The results obtained with the two different methods are fully consistent and agree with previous thermal expansion studies performed at ambient pressure. The resulting thermal equation of state can be described using a third-order Birch–Murnaghan formalism with a Berman thermal-expansion model. The present equation of the state of iridium can be used as a reliable primary pressure standard for static experiments up to 80 GPa and 3100 K.
    [Show full text]
  • The Radiochemistry of Iridium-- +- -:, G
    ———..————- !546.8 L472ra NAS-NS 3045 .c.8 THE RADIOCHEMISTRY OF IRIDIUM-- +- -:, G. W. Leddicotte ‘1 Oak Ridge National Laboratory Oak Ridge, Tennessee October 1961 .- .- .. --.—- ---- -. ---- -. —.-. .- ---- ---- --- .- .. .- .— .— –. —-. .— —- -- -—. I -.. - -.. I ..-.- . -. I .. .. .. -- 1.- REPORT selection aids Pinpointing R & D rej9G7t8for hdu.st~ Clearinghouse, Sprhgfleld, Va, 22151 GOVERNMENT-WIDE INDEX—SEMI-MONTHLY GUIDE TO FEDERAL SCIIZNTIYIC AND TECH- NICAL REPORTS. ANNUAL SUBSCRIPTION S22.00 ($27.50 FOREIGN MAILING). SINGLE COPY $3.00. U.S. GOVERNMENT RESEARCH AND DEVELOPMENT REPORTS_EMI-MONTHLY JOURNAL ANNOUNCING R&D REPORTS. ANNUAL SUBSCRIPTION 830.00 ($27A0 FOREIGN MAILING). SINGLE COPY $3.00. FAST ANNOUNCEMENT SERVICE—SUMMARIES OF SELIZCTED R&D REPORTS MAILED ❑ Y INDUSTRIAL CATEGORIES, SS.00 ANNUAL SUBSCRIPTION. WRITE FOR AN APPLICATION FORM. DOCUMENT PRICES~FFECTIVE JANUARY 1, 19s7 THE CLEARINGHOUSE CHANGED ITS PRICING POLICY FOR DOCUMENT SALES FROM A SLIDING PRICE SCALE BASED ON DOCUMENT SIZE TO A SINGLE PRICE FOR DOCUMENTS SOLD. THE NEW DOCUMENT PRICE FOR A PAPER COPY (HARD COPY - HC) DOCUMENT IS $3.00. THE NEW PRICE FOR A MICROFICHE (MFI COPY IS s.ss PER DOcuMENT. THEsE PRICES ALSO ApPLY TO DOCUMENTS ANNOUNCED PRIOR TO JANUARY 1, 1967. THE NEW UNIT PRICES ARE BELOW THE PREVIOUS AVERAGE PRICES OF DOCUMENTS SOLD BY THE CLEARINGHOUSE. EFFICIENCIES IN ORDER PROCESSING RESULTING FROM THE SINGLE PRICE POLICY MAKE THE LOWER AVERAGE PRICE POSSIBLE. THE CLEARINGHOUSE SEL15 COUPONS FOR THE PURCHASE OF DOCUMENTS WHICH SIMPLIFY ORDERING AND HANDLING ❑ Y BOTH THE CLEARINGHOUSE AND ITS CUSTOMERS, PERMITTING THE CLEARINGHOUSE TO GIVE FASTER SERVICE ON DOCUMENT REQUESTS. THE COUPON IS A TABULATING CARD WITH A FACE VALUE OF THE PURCHASE PRICE OF A CLEARINGHOUSE DOCUMENT (S3.00 FOR HC, $.SS FOR MF).
    [Show full text]
  • Periodic Table 1 Periodic Table
    Periodic table 1 Periodic table This article is about the table used in chemistry. For other uses, see Periodic table (disambiguation). The periodic table is a tabular arrangement of the chemical elements, organized on the basis of their atomic numbers (numbers of protons in the nucleus), electron configurations , and recurring chemical properties. Elements are presented in order of increasing atomic number, which is typically listed with the chemical symbol in each box. The standard form of the table consists of a grid of elements laid out in 18 columns and 7 Standard 18-column form of the periodic table. For the color legend, see section Layout, rows, with a double row of elements under the larger table. below that. The table can also be deconstructed into four rectangular blocks: the s-block to the left, the p-block to the right, the d-block in the middle, and the f-block below that. The rows of the table are called periods; the columns are called groups, with some of these having names such as halogens or noble gases. Since, by definition, a periodic table incorporates recurring trends, any such table can be used to derive relationships between the properties of the elements and predict the properties of new, yet to be discovered or synthesized, elements. As a result, a periodic table—whether in the standard form or some other variant—provides a useful framework for analyzing chemical behavior, and such tables are widely used in chemistry and other sciences. Although precursors exist, Dmitri Mendeleev is generally credited with the publication, in 1869, of the first widely recognized periodic table.
    [Show full text]
  • Investigation of the Platinum Metals: IV. Determination of Iridium In
    .. INVESTIGATIONS ON THE PLATINUM METALS 1 IV. DETERMINATION OF IRIDIUM IN PLATINUM ALLOYS BY THE METHOD OF FUSION WITH LEAD. By Raleigh Gilchrist. ABSTRACT. A study has been made of the analytical details of the Deville and Stas method for the determination of iridium in platinum alloys containing from o. i to 20 per cent of iridium. Specially prepared alloys made from, highly purified metals were used in the investigation. It was found that the concentration of nitric acid, the concen- tration of aqua regia, the proportion of lead, and the time and the temperature of the lead fusion can be varied over a wide range without affecting the determination. The observations of Deville and Stas that palladium and rhodium have no effect upon the determination and that ruthenium separates quantitatively with the iridium were confirmed. In addition, gold was found not to interfere. Iron sepa- rates nearly quantitatively with the iridium as observed by Deville and Stas. A method for the separation of iron from the iridium was tested and found to give satisfactory results. The loss in weight of crystalline iridium during the ignition periods is insignificant and the weight of crystalline iridium is not affected by heating and cooling in an atmosphere of hydrogen. Spectrographic examination of samples of iridium from analysis showed that neither platinum nor lead was present in sufficient quantities to affect the determination. The iridium results tend to be low by a variable but usually small amount. One factor in this error is a slight solution of iridium by aqua regia. A modified procedure for the method is offered, which combines the optimum conditions for speed and accuracy in the various details of manipulation.
    [Show full text]
  • The Freezing Point of Iridium
    RP568 THE FREEZING POINT OF IRIDIUM By F. Henning 1 and H. T. Wensel 2 ABSTRACT The ratio of brightness for red light of a black < body immersed in freezing indium to that of a similar black body immersed in freezing gold was measured both directly and indirectly. The indirect method consisted in determining the ratio of brightness at the iridium and platinum freezing points and calculating the result from the previously determined platinum to gold ratio. The two methods, agreeing with each other within experimental errors, yielded a value for the iridium to gold ratio of 4,380 at wave length 0.652 p. This fixes the freezing point of iridium on the International Temperature Scale as 2,454° C. CONTENTS Pari' I. Introduction 809 II. Previous work 810 III. Present work 813 1. The iridium 813 2. The furnace and crucible Ml 3. Method of observation 81 1 4. Determination of effective wave length Ml IV. Results M7 V. Summary 819 VI. Acknowledgments 819 VII. Appendix. Preparation and purity of iridium 819 I. INTRODUCTION In making an accurate determination of the freezing or melting temperature of a pure metal, one of the objects is usually a more accu- rate establishment of the temperature scale in practical use by pro- viding an additional known fixed point at which temperature measur- ing equipment may be checked. In the present work, however, this item was of comparatively small importance. The extremely high cost of the metal, the difficulty of purifying it to the required degree, and the difficulties encountered in melting the metal under suitable conditions prohibit its use as a secondary thermometric fixed point except in very unusual cases.
    [Show full text]
  • Periodic Table P J STEWART / SCIENCE PHOTO LIBRARY PHOTO SCIENCE / STEWART J P
    Periodic table P J STEWART / SCIENCE PHOTO LIBRARY PHOTO SCIENCE / STEWART J P 46 | Chemistry World | March 2009 www.chemistryworld.org Periodic change The periodic table, cherished by generations of chemists, has steadily evolved over time. Eric Scerri is among those now calling for drastic change The periodic table has become recurrences as vertical columns or something of a style icon while In short groups. remaining indispensable to chemists. In its original form The notion of chemical reactivity Over the years the table has had the periodic table was is something of a vague one. To make to change to accommodate new relatively simple. Over this idea more precise, the periodic elements. But some scientists the years, extra elements table pioneers focused on the propose giving the table a makeover have been added and the maximum valence of each element while others call for drastic changes layout of the transition and looked for similarities among to its core structure. elements altered these quantities (see Mendeleev’s More than 1000 periodic systems Some call for drastic table, p48). have been published since the table rearrangements, The method works very well for Russian chemist Dimitri Mendeleev perhaps placing hydrogen the elements up to atomic weight developed the mature periodic with the halogens. 55 (manganese) after which point system – the most fundamental A new block may be it starts to fall apart. Although natural system of classification needed when chemists there seems to be a repetition in the ever devised. (Not to mention the can make elements in highest valence of aluminium and hundreds if not thousands of new the g-block, starting at scandium (3), silicon and titanium systems that have appeared since the element 121 (4), phosphorus and vanadium (5), advent of the internet.) and chlorine and manganese (7), Such a proliferation prompts this is not the case with potassium questions as to whether some tables and iron.
    [Show full text]
  • Reduced-Graphene-Oxide with Traces of Iridium Or Gold As Active Support for Pt Catalyst at Low Loading During Oxygen Electroreduction
    Reduced-Graphene-Oxide with Traces of Iridium or Gold as Active Support for Pt Catalyst at Low Loading during Oxygen Electroreduction P. J. Kuleszaa, B. Dembinskaa, S. Zoladeka, I. A. Rutkowskaa, K. Miecznikowskia, E. Negrob, V. Di Notob aDepartment of Chemistry, University of Warsaw, Pasteura 1, PL-02-093 Warsaw, Poland bDepartment of Industrial Engineering, Università degli Studi di Padova in Department of Chemical Sciences, Via Marzolo 1, 35131 Padova (PD) Italy Chemically-reduced graphene-oxide-supported gold or iridium nanoparticles are considered here as active carriers for dispersed platinum with an ultimate goal of producing improved catalysts for electroreduction of oxygen in acid medium. Comparison is made to the analogous systems not utilizing reduced graphene oxide. High electrocatalytic activity of platinum (loading up to 30 µg cm-2) dispersed over the reduced-graphene oxide-supported Au (up to 30 µg cm-2) or Ir (up to 1.5 µg cm-2) nanoparticles toward reduction of oxygen has been demonstrated using cyclic and rotating ring-disk electrode (RRDE) voltammetric experiments. Among important issues are possible activating interactions between gold and the support, as well as presence of structural defects existing on poorly organized graphitic structure of reduced graphene oxide. The RRDE data are consistent with decreased formation of hydrogen peroxide. Introduction There has been growing interest in the field of oxygen electroreduction, particularly with respect to potential applications in the science and technology of low- temperature fuel cells (1-11). Obviously, many efforts have been made to develop suitable alternative electrocatalysts efficient enough to replace electrocatalysts based on scarce strategic elements such as platinum-group metals (5,6,8,9,12,13).
    [Show full text]