Dielectric Materials: Properties and Applications
Content
1. Dielectrics : Properties 2. Fundamental definitions and Properties of electric dipole 3. Various polarization mechanisms involved in dielectric : 3.1 Electronic polarization, 3.2 Ionic polarization, 3.3 Orientation polarization, 3.4 Space charge polarization; 3.5 Total polarization 4. Active and Passive Dielectrics 5. Frequency and Temperature on Polarization of Dielectrics : 5.1 Frequency Dependence, 5.2 Temperature Dependence, 6. Internal field or Local field : 6.1 Definition, 6.2 Derivation, 6.3 Clausius – Mosoti Equation 7. Dielectrics and Loss Tangent; 7.1 Loss in purified gas; 7.2 Loss in commercial dielectric ; 7.3 Power loss 8. Dielectric Breakdown: 8.1 Types of dielectric breakdown; 8.2 Remedies for breakdown mechanisms 9. General Applications 10. Applications of dielectric materials : 10.1 Dielectrics in capacitors, 10.2 Insulating materials in transformers 11. Ferro-electrics : 11.1 Properties, 11.2 Applications
1 3/23/2018
Understanding Dielectric:
• Solids which have an energy gap of 3eV or more are termed as insulators. • In these materials, it is almost not possible to excite the electrons from the valence band to conduction band by an applied field. • Generally dielectrics are also called as insulators, thereby poor conductors of electricity. However they allow movement of some electrons at abnormally high temperatures, causing a small flow of current. • Dielectrics are non-metallic materials of high specific resistance ρ, negative temperature coefficient of resistance (-α), large insulation resistance. • Insulation resistance will be affected by moisture, temperature, applied electric field and age of dielectrics.
Understanding Dielectric:
• Dielectric materials are electrically non-conducting materials such as glass, ebonite, mica, rubber, wood and paper. • All dielectric materials are insulating materials. • The difference between a dielectric and an insulator lies in their applications. • If the main function of non-conducting material is to provide electrical insulation, then they are called as insulator. On the other hand, if the main function of non-conducting material is to store electrical charges then they are called as dielectrics.
2 3/23/2018
Properties
• Generally, the dielectrics are non-metallic materials of high resistivity. • They have a very large energy gap (more than 3eV). • All the electrons in the dielectrics are tightly bound to their parent nucleus. • As there are no free electrons to carry the current, the electrical conductivity of dielectrics is very low. • They have negative temperature coefficient of resistance and high insulation resistance.
Fundamental Definitions And Properties Electric Dipole
• A system consisting of two equal and opposite charges n(+q, -q) separated by a distance (d) is called an electric dipole.
DIPOLE MOMENT (P) • The product of the magnitude of the charge (q) and distance between two charges (d) is called as dipole moment. • Dipole moment P = qd (coulomb-metre)
3 3/23/2018
Fundamental Definitions And Properties Electric Dipole PERMITTIVITY (ε) • The permittivity represents the dielectric property of a medium. It indicates easily polarizable nature of material. Its unit is farad/metre
DIELECTRIC CONSTANT (εr ) • A dielectric characteristic of a material is determined by its dielectric constant. It is a measure of polarisation of the dielectrics. Definition • It is the ratio between absolute permittivity of the medium (ε) and permittivity of free space (εo).
Dielectric constant = Absolute permittivity (ε) / Permittivity of free space (εo ) εr = ε / εo
Fundamental Definitions And Properties Electric Dipole POLARIZATION Definition • The process of producing electric dipoles inside the dielectric by the application of an external electrical field is called polarization in dielectrics. POLARISABILITY (α) It is found that the average dipole moment field (E). μ = α E Where (α) is the polarisability. α = μ / E Polarisability is defined as the ratio of average dipole moment to the electrical field applied. Its unit is farad m2 .
4 3/23/2018
5 3/23/2018
Active and Passive Dielectrics The dielectric materials can be classified into active and passive dielectric materials. i. Active dielectrics When a dielectric material is kept in an external electric field, if it actively accepts the electricity, then it is known as active dielectric material. Thus, active dielectrics are the dielectrics, which can easily adapt themselves to store the electrical energy in it. ii. Passive dielectrics Passive dielectrics are the dielectrics, which restrict the flow of electrical energy in them. So, these dielectrics act as insulators. Examples: All insulating materials such as glass, mica, rubber etc.,
6 3/23/2018
7 3/23/2018
Basically, there are four mechanisms of polarization: Electronic or Atomic Polarization This involves the separation of the centre of the electron cloud around an atom with respect to the centre of its nucleus under the application of electric field (see (a) in figure below). Ionic Polarization This happens in solids with ionic bonding which automatically have dipoles but which get cancelled due to symmetry of the crystals. Here, external field leads to small displacement of ions from their equilibrium positions and hence inducing a net dipole moment (see (b)). Dipolar or Orientation Polarization This is primarily due to orientation of molecular dipoles in the direction of applied field which would otherwise be randomly distributed due to thermal randomization (see (c and d)) and finally Interface or Space Charge Polarization This involves limited movement of charges resulting in alignment of charge dipoles under applied field. This usually happens at the grain boundaries or any other interface such as electrode-material interface (see (e and f))
8 3/23/2018
9 3/23/2018
10 3/23/2018
11 3/23/2018
12 3/23/2018
Dielectrics and Loss Tangent
13 3/23/2018
14 3/23/2018
15 3/23/2018
16 3/23/2018
17 3/23/2018
18 3/23/2018
19 3/23/2018
20 3/23/2018
21 3/23/2018
Ferroelectric – A material that shows spontaneous and reversible dielectric polarization.
22 3/23/2018
23 3/23/2018
24 3/23/2018
Piezoelectric –
A material that develops voltage upon the application of a stress and develops strain when an electric field is applied.
25 3/23/2018
©2003 Brooks/Cole, a division of Thomson Learning, Inc. Thomson Learning™ is a trademark used herein under license.
The (a) direct and (b) converse piezoelectric effect. In the direct piezoelectric effect, applied stress causes a voltage to appear. In the converse effect (b), an applied voltage leads to development of strain.
Direct piezoelectric Reverse (converse) effect piezoelectric effect
26 3/23/2018
27 3/23/2018
E
E
28 3/23/2018
Direct piezoelectric effect
P = d
P = d d o d: Piezoelectric coupling coefficient (piezoelectric charge coefficient)
Table: The piezoelectric constant d (longitudinal) for selected materials Piezoelectric constant d Material (C/N = m/V) Quartz 2.3 x 10-12 -12 BaTiO3 100 x 10 -12 PbZrTiO6 250 x 10 -12 PbNb2O6 80 x 10
29 3/23/2018
PZT: PbZrO3-PbTiO3 solid solution or lead zirconotitanate
30 3/23/2018
Table: Properties of commercial PZT ceramics
Property PZT-5H PZT4 (soft) (hard) Permittivity ( at 1 kHz) 3400 1300 Dielectric loss (tan at 1 kHz) 0.02 0.004
Curie temperature (Tc, C) 193 328 Piezoelectric coefficients (10-12 m/V)
d33 593 289
d31 -274 -123
d15 741 496 Piezoelectric coupling factors
k33 0.752 0.70
k31 -0.388 -0.334
k15 0.675 0.71
Table: Measured longitudinal piezoelectric coupling coefficient d, measured relative dielectric constant , calculated piezoelectric voltage coefficient g and calculated voltage change resulting from a stress change of 1 kPa for a specimen thickness of 1 cm in the direction of polarization.
Voltage change Material d (10-13 m/V)* † g (10-4 m2/C)† (mV)† Cement paste 0.659 0.031 35 2.2 2.2 (plain) Cement paste with 208 16 2700 8.7 8.7 steel fibers and PVA Cement paste with 3.62 0.40 49 8.5 8.5 carbon fibers PZT 136 1024 15 15
*Averaged over the first half of the first stress cycle †At 10 kHz
31 3/23/2018
Piezopolymer
Moonie
Cymbal
Composites with piezoelectric/ferroelectric material sandwiched by metal faceplates fo enhancing the piezoelectric coupling coefficient
32 3/23/2018
Pyroelectric –
The ability of a material to spontaneously polarize and produce a voltage due to changes in temperature.
dP d Material p(10-6 C/m2.K) p o , dT dT BaTiO3 20 PZT 380 p = pyroelectirc coefficient PVDF 27 P = polarization Cement paste 0.002
Px V = ( -1) o
Voltage sensitivity
dV P dx x dP = d ( -1) o d ( 1) o d Compliance Piezoelectric coupling coefficient d
33 3/23/2018
Piezoelectric composite
• When any material undergoes polarization (due to an applied electric field), its ions and electronic clouds are displaced, causing the development of a mechanical strain in the material. polarization. • This phenomenon is known as the electrostriction.
34 3/23/2018
Examples of ceramic capacitors. (a)Single-layer ceramic capacitor (disk capacitors). (b) Multilayer ceramic capacitor (stacked ceramic layers).
Types of Dielectric Materials Dielectric materials can be divided into following groups: • Solid Dielectrics - are of following types: – • Mica – is inorganic material and is crystalline in nature. – • Glass – is inorganic material made by fusion of different oxides. – • Rubber – is a organic polymer, which can be natural or artificial. – • Ceramic – is non-metallic organic compound such as silicates
35 3/23/2018
Types of Dielectric Materials
Liquid Dielectric – includes following: • Mineral Insulating Oils – obtained from crude petroleum & have high oxidation resistance. • Synthetic Insulating oil – are very much resistant to oxidation & fire hazards. • Miscellaneous Insulating oils – Vaseline, vegetable oils, silicon oils belongs to this. Gaseous Dielectric – includes • Air • Nitrogen • Sulphur hexafluoride • Inert gases
36