Britt Glaze Recipes

Total Page：16

File Type：pdf, Size：1020Kb

Download full-text PDF Read full-text
Britt Glaze Recipes recipes STEVE IRVINE RED Cone 10 NC-4 Soda Feldspa . 41 .72 % Silica . 22 .25 Talc . 7 .34 EPK Kaolin . 6 .45 Bone Ash . 10 .23 Whiting . 6 .45 Magnesium Carbonate Light . 5 .56 100 .00 % SELSOR RED Cone 6 Gerstley Borate . 12 .5 % Whiting . 10 .4 Nepheline Syenite . 56 .3 Silica . 20 .8 100 % Add: Tin Oxide . 1 .6 % Copper Carbonate . 0 .8 % Red Iron Oxide . 0 .1 % jeff’s red Cone 10 reduction Custer Feldspar . 41 .9 % Silica . 26 .2 Whiting . 8 .4 Frit 3134 . 8 .7 Zinc Oxide . 1 .7 Barium Carbonate . 4 .4 Dolomite . 8 .7 100 % Add: Bentonite . 1 .0 % Copper Carbonate . 0 .5 BURGUNDY/RED CHROME RED Cone 6 Cone 6 Gerstley Borate . 8 % Gerstley Borate . 21 % Talc . 4 Whiting . 20 Whiting . 21 Nepheline Syenite . 16 Ferro Frit 3134 . 9 EPK Kaolin . 11 Custer Feldspar . 31 Silica . 32 EPK Kaolin . 9 100 % Silica . 18 Add: Tin Oxide . 5 .00 % 100 % Chrome Oxide . 0 .15 % Burgundy Red Chrome Red with Add: Tin Oxide . 5 .00 % 0.25% Cobalt Chrome Oxide . 0 .20 % Carbonate ODYSSEY BASE Cone 6 Gerstley Borate . 20 % Whiting . 10 Nepheline Syenite . 30 EPK Kaolin . 10 Silica . 30 100 % A standard base from the Odyssey Center in Asheville, North Carolina . Contains high boron, calcium, and sodium, gives bright, glossy, transparent colors . Odyssey Base with Odyssey Base with Odyssey Base with Odyssey Base with 0.15% chrome 0.5% chrome 1.0% chrome 2.0% chrome RANDY’S BASE Cone 6 Gerstley Borate . 31 .7 % Talc . 3 .8 F-4 Feldspar . 19 .8 EPK Kaolin . 5 .0 Silica . 29 .7 100 .0 % An excellent and popular base (originally from Randy’s Red) . Contains a lot of boron and low alumina, gives bright, glossy, trans- parent colors . Randy’s Base with Randy’s Base with 0.15% Randy’s Base with Randy’s Base with 0.15% chrome chrome on stoneware 0.5% chrome 1.0% chrome REITZ GREEN GLAZE EMILy’s PurPLE Cone 9–10 Cone 9–10 Gerstley Borate . 2 % Dolomite . 7 % Whiting . 5 Gerstley Borate . 12 Nepheline Syenite . 70 Talc . 15 Petalite . 15 Custer Feldspar . 41 Ball Clay . 8 Ball Clay . 5 100 % Silica . 20 Add: Rutile . 2 % 100 % Cobalt Carbonate . 1 % Add: Bentonite . 2 % Black Cobalt Oxide . 2 % Tin Oxide . 2 % FLOATING BLUE GLAZE (Cone 6, oxidation) Gerstley Borate . 26 % Nepheline Syenite . 48 Edgar Plastic Kaolin (EPK) . 6 Flint (325 mesh) . 20 100 % Add: Cobalt Oxide . 1 % LightRutile . 4 % Red Iron Oxide . 2 % From Jeff Zamek, Ceramics Monthly, October 2001 . Left: SG-259 - A silky matt barium copper blue. Right: SG-259 with strontium carbonate. The surface feel is very similar, perhaps a little smoother in the strontium glaze. SG-259 OPAQUE BLUE MATT SG-259 OPAQUE BLUE MATT (Cone 10) WITH STRONTIUM Barium Carbonate . 38 .4 (Cone 10) Nepheline Syenite . 48 .0 Strontium Carbonate . 31 .9 Tennessee Ball Clay #10 . 6 .1 Nepheline Syenite . 53 .1 Silica (Flint) . 7 .5 Tennessee Ball Clay #10 . 6 .7 100 .0 % Silica (Flint) . 8 .3 Add: Copper Carbonate . 4 .0 % 100 .0 % Bentonite . 1 .0 % Add: Copper Carbonate . 4 .0 % Bentonite . 1 .0 % PINNELL CELADON Cone 10 Custer Feldspar . 24 .50 % Silica . 34 .32 Whiting . 19 .61 Grolleg Kaolin . 19 .61 Barium Carbonate . .. 1 .96 100 % Add: Tin Oxide . 1 .00 % Barnard Slip . .. 3 .00 % TEA DUST Cone 6, reduction Custer Feldspar . 40 % Frit 134 . 9 Whiting . 16 Talc . 9 EPK Kaolin . 10 Silica (Flint) . 16 100 % Add: Red Iron Oxide . 10 % BASIC CELADON Cone 6 Custer Feldspar . 25 % Silica . 25 Whiting . 25 EPK Kaolin . 25 100 % Add: Red Iron Oxide . 3 .00 % HAMADA RUST Cone 9-10 reduction Custer Feldspar . 77 .0 % Silica . 0 .1 Whiting . 6 .2 Kaolin . 4 .3 Gerstley Borate . 12 .4 100 % Add: Red Iron Oxide . .. 7 .5 % Base Only Tangerine Yellow Blue Blue Green Turqoise Blue Light Green Lavender Ochre Dark Green Medium Brown Charcoal Gray SHERMAN’s SATIN MATT Blue Dark Green (FATTY MATT!) Add: Cobalt Oxide . 0 .5–2% Add: Copper Carbonate . 3 % Blue Green cone 6 oxidation Medium Brown Add: Chrome Oxide . 1 % Dolomite . 10 % Add: Red Iron Oxide . 5 % Talc . 15 Cobalt Oxide . 1 % Charcoal Gray Nepheline Syenite . 35 Turquoise Blue Add: Mason Stain 6600 . 5 % Ferro Frit 3124 . 10 Add: Mason Stain 6373 . 5 % EPK Kaolin . 15 Light Green The magnesium in this glaze can cause cobalt Silica . 15 Add: Mason Stain 6265 . 5 % to lean toward the purple side of blue . You can 100 % see this even in the Turquoise Blue (MS 6373) Tangerine Lavender Add: Mason Stain 6304 . 5 % stain . And even though there is a fair amount of Add: Mason Stain 4200 . 5 % calcium in this glaze, iron will pretty much stay Ochre Yellow brown rather than warming up to red/orange . Add: Mason Stain 4250 . 5 % Add: Mason Stain 6129 . 5 % LINDA ARBUCKLE MAJOLICA (Cone 03, oxidation) Ferro Frit 3124 . 65 .8 % F-4 Feldspar (sub Minspar 200) . 17 .2 Nepheline Syenite . 6 .2 EPK Kaolin . 10 .8 100 % Add: Tin Oxide . 4 .0 % Zircopax . 9 .0 % Bentonite . 2 .0 % This is a smooth, white, opaque glaze that does not move during firing . It may crawl if thick in corners or pinhole over rough-trimmed surfaces . Add ½–3 tsp . Epsom salts to 5 gal- lons of glaze to flocculate if needed (for less settling and better application) . Colorants with flux are usually applied in a thin wash to the raw glaze surface . RAKU TURQUOISE (Cone 018, post-firing reduction) P-25 . .. 42 .5 % Ferro Frit 3134 . 27 .4 Silica . 14 .0 Lithium carbonate . 9 .8 EPK Kaolin . 6 .3 100 % Add: Copper Carbonate . 3 .0-4 .5 % Bentonite . 2 .0 %.
Load more

Recommended publications
  • An Experiment with Mineral Pigments in a Prepared Frit
    Central Washington University ScholarWorks@CWU All Master's Theses Master's Theses 1951 An Experiment With Mineral Pigments in a Prepared Frit Cecelia Long Central Washington University Follow this and additional works at: https://digitalcommons.cwu.edu/etd Part of the Art Education Commons, and the Educational Methods Commons Recommended Citation Long, Cecelia, "An Experiment With Mineral Pigments in a Prepared Frit" (1951). All Master's Theses. 56. https://digitalcommons.cwu.edu/etd/56 This Thesis is brought to you for free and open access by the Master's Theses at ScholarWorks@CWU. It has been accepted for inclusion in All Master's Theses by an authorized administrator of ScholarWorks@CWU. For more information, please contact [email protected]. AN EXPERIMENT WITH MINBi.ALJ:J>IGMENTS IN A PREPARED FRI:r by Cecelia Long A thesis submitted in partial fulfillment of the requirements for the degree of Master of Fiiucation, in the Graduate School of the Central Washington College of Fii.ucation August 1951 i A thesis submitted in partial fulfillment of the requirements for the degree of Master of Education in the Graduate School of the Central Washington College of Education. Approved: Thesis Chairman _____________________________ Dr. Charles W. Saale ___________________________ Mr. Glen Hogue _____________________________ Miss Lillian Bloomer Date:_____________ ii ACKNOWLEDGMENTS Due acknowledgment is made to Dr. Charles W. Saale for assistance with the organization and preparation of the manuscript. My thanks are due to Mr. Glenn Hogue for guidance in preparing and making this experiment. iii TABLE OF CONTENTS CHAPTER PAGE I Introduction •••••••••••••••••••••••••• 1 II Delineation of Materials and Review of Related Experiments..................
    [Show full text]
  • The Analysis and Reconstruction of Islamic Glass-Frit Ceramics, And
    Article: The analysis and reconstruction of Islamic glass-frit ceramics, and comparative methods of desalination Author(s): Richard Barden Source: Objects Specialty Group Postprints, Volume Three, 1995 Pages: 64-69 Compilers: Julie Lauffenburger and Virginia Greene th © 1996 by The American Institute for Conservation of Historic & Artistic Works, 1156 15 Street NW, Suite 320, Washington, DC 20005. (202) 452-9545 www.conservation-us.org Under a licensing agreement, individual authors retain copyright to their work and extend publications rights to the American Institute for Conservation. Objects Specialty Group Postprints is published annually by the Objects Specialty Group (OSG) of the American Institute for Conservation of Historic & Artistic Works (AIC). A membership benefit of the Objects Specialty Group, Objects Specialty Group Postprints is mainly comprised of papers presented at OSG sessions at AIC Annual Meetings and is intended to inform and educate conservation-related disciplines. Papers presented in Objects Specialty Group Postprints, Volume Three, 1995 have been edited for clarity and content but have not undergone a formal process of peer review. This publication is primarily intended for the members of the Objects Specialty Group of the American Institute for Conservation of Historic & Artistic Works. Responsibility for the methods and materials described herein rests solely with the authors, whose articles should not be considered official statements of the OSG or the AIC. The OSG is an approved division of the AIC but does not necessarily represent the AIC policy or opinions. THE ANALYSIS AND RECONSTRUCTION OF ISLAMIC GLASS-FRIT CERAMICS, AND COMPARATIVE METHODS OF DESALINATION Richard Barden The Freer Collection The Freer Gallery of Art has a collection of medieval Islamic glazed glass-frit ceramics, from Raqqa, Syria.
    [Show full text]
  • Revisiting the Beginnings of Tin-Opacified Islamic Glazes
    Journal of Archaeological Science 57 (2015) 80e91 Contents lists available at ScienceDirect Journal of Archaeological Science journal homepage: http://www.elsevier.com/locate/jas Revisiting the beginnings of tin-opacified Islamic glazes * Michael Tite a, , Oliver Watson b, Trinitat Pradell c, Moujan Matin a, Gloria Molina c, Kelly Domoney d, Anne Bouquillon e a Research Laboratory for Archaeology and the History of Art, Dyson Perrins Building, South Parks Road, Oxford OX1 3QY, UK b Khalili Research Centre for the Art and Material Culture of the Middle East, 3, St John Street, Oxford OX1 2LG, UK c Physics Department and Center for Research in Nano-Engineering, Universitat Politecnica de Catalunya, C/Esteve Terrades 8, 08860 Castelldefels, Barcelona, Spain d Centre for Archaeological and Forensic Analysis, Cranfield University, Shrivenham SN6 8LA, UK e C2RMF, Palais du Louvre, 14, quai François Mitterrand, 75001 Paris, France article info abstract Article history: The generally accepted theory is that the demand for Islamic glazed pottery started in Abbasid Iraq in the Received 12 September 2014 9th century AD with the production of a range of glazed wares in response to the import of Chinese Received in revised form stonewares and porcelains. However, Oliver Watson has recently proposed that the demand for Islamic 22 January 2015 glazed pottery first occurred in Egypt and Syria in the 8th century AD resulting in the production of Accepted 3 February 2015 opaque yellow decorated wares. Using a combination of SEM analysis of polished cross-sections, and Available online 14 February 2015 surface analysis using hand-held XRF or PIXE, Coptic Glazed Ware from Egypt, Yellow Glazed Ware from Syria, and comparable wares from Samarra, Kish and Susa have been analysed.
    [Show full text]
  • Frit Slurrys!
    Here, at Creative Paradise Inc, weFRIT have been playing SLURRYS! around with dierent ways to use frit on glass. We have come up with a cool and unique way to blend frit colors, and all it involves is a splash of water powdered frit! In the following tutorials we will show you how we made all the fun and interesting color patterns and mixes in the samples pictured. It can be a messy process but the unique results speak for them selves! For the rst project, we blended our frit slurry’s on a Materials used: square of Double ick Clear COE96 sheet glass, and COE96 8.5” x 8.5” Double ick Clear Sheet Glass then slumped it on our GM 142 Quad Swoop Slump- All COE96 Frits: all in one ring! F1 Black Opaque F1 Deep Purple Transparent F1 Bronze Transparent F1 Turns Pink Striker Transparent F1 Medium Amber Transparent F1 Transparent Orange Water and a spray bottle of water Paper Towels Paper Cups/ small Mixing bowls Plastic knife, Spoon ZYP/Boron Nitride Glass Separator Spray CPI GM142 Mold Step 1. Cut a 8.25” x 8.25” square out of COE96 Transparent Glass. Clean the square of glass with glass cleaner before you begin to use it. Image 1 Step 2. *Create a Bronze frit slurry. With a How to make the frit slurry mix: Put the desired color spoon, place some of the mixture into the middle *of frit you want into a paper cup (or other mixing of the square. Spread the Bronze slurry to create container)and add a splash of water.
    [Show full text]
  • Islamic Ceramics, Indelible Creations: Assessing and Preserving the Scripps Collection Josephine Ren
    Claremont Colleges Scholarship @ Claremont Scripps Senior Theses Scripps Student Scholarship 2019 Islamic Ceramics, Indelible Creations: Assessing and Preserving the Scripps Collection Josephine Ren Recommended Citation Ren, Josephine, "Islamic Ceramics, Indelible Creations: Assessing and Preserving the Scripps Collection" (2019). Scripps Senior Theses. 1353. https://scholarship.claremont.edu/scripps_theses/1353 This Open Access Senior Thesis is brought to you for free and open access by the Scripps Student Scholarship at Scholarship @ Claremont. It has been accepted for inclusion in Scripps Senior Theses by an authorized administrator of Scholarship @ Claremont. For more information, please contact [email protected]. Ren 1 TABLE OF CONTENTS Acknowledgements……………………………………………...………………………2 Introduction……………………………………………………………………………...3 Chapter 1. Surveying the Scripps Islamic Ceramics…………………………………….9 ​ ​ Condition Reports, Formal Analyses, and Contextual Backgrounds Appendix 1……………………………………………………………………………...39 Figures Chapter 2. Ethics, Problems, and Proposals for Future Collections Care……………...64 ​ ​ Preventive Conservation and Prioritization of Certain Wares Appendix 2……………………………………………………………………………...80 Figures Conclusion……………………………………………………………………………....87 Bibliography…………………………………………………………………………….90 Ren 2 ACKNOWLEDGEMENTS I wish to begin by thanking my readers for all their time, mental energy, and support in overseeing this project. These colleges are fortunate to have you and your expertise. Professor Blessing has been key
    [Show full text]
  • Analyzing Ancient Egyptian Faience
    THE PENNSYLVANIA STATE UNIVERSITY SCHREYER HONORS COLLEGE DEPARTMENTS OF MATERIALS SCIENCE AND ENGINEERING AND ART HISTORY EXPLORING ANCIENT EGYPTIAN FAIENCE WITH NANOTECHNOLOGY: COMPOSITIONAL MAPPINGS, MICROSTRUCTURE ANALYSIS, AND MODERN APPLICATIONS ELYSSA IRIS OKKELBERG Summer 2011 A thesis submitted in partial fulfillment of the requirements for baccalaureate degrees in Materials Science and Engineering and Art History with interdisciplinary honors in Materials Science and Engineering and Art History Reviewed and approved∗ by the following: Paul Howell Professor of Metallurgy Thesis Supervisor Honors Advisor Elizabeth Walters Associate Professor of Art History Honors Advisor Digby MacDonald Distinguished Professor of Materials Science and Engineering Faculty Reader ∗Signatures are on file in the Schreyer Honors College. Abstract This thesis investigated Egyptian faience, an ancient ceramic material that consists of granular quartz or sand coated with an alkali-based glaze. Of interest is the pro- duction process of faience, in particular the raw materials and the glazing method. Previous investigations examined the production process using compositional and microstructural data from ancient and replicate faience. This study confirmed prior results by investigating faience beads produced in Abydos, Egypt during the 22nd Dynasty (c. 940–720 BC). Furthermore, this investigation improved upon earlier works by creating compositional mappings and analyzing previously over- looked parts of faience. Moreover, modern applications for faience technology were explored. i Table of Contents Abstract i List of Figures iv List of Tables vi Acknowledgments vii Chapter 1 Egyptian Faience 1 1.1 Background ............................... 1 1.2 Production ............................... 3 1.2.1 Rawmaterials.......................... 4 1.2.2 Shaping ............................. 7 1.2.3 GlazingMethod......................... 8 1.2.4 Firing .............................
    [Show full text]
  • A Recent Evaluation of the Defense Waste Processing Facility (DWPF
    WM2011 Conference, February 27 – March 3, 2011, Phoenix, AZ Process Enhancements to Improve Overall Throughput in the Defense Waste Processing Facility at the Savannah River Site - 11458 Jonathan M. Bricker*, Terri L. Fellinger*, Dale J. Hutsell*, Robert C. Hopkins*, Bradley R. Pickenheim†, Erich K. Hansen†, David K. Peeler†, Michael E. Stone†, Wing K. Kot◊, Marek Brandys◊, Robert K. Mohr◊, Ian L. Pegg◊, Holly K. Pasieka£, Innocent Joseph£, and Glenn A. Diener£ * Savannah River Remediation, Aiken, South Carolina, 29808 † Savannah River National Laboratory, Aiken, South Carolina, 29808 ◊ Vitreous State Laboratory, The Catholic University of America, Washington, DC, 20064 £ EnergySolutions, Inc., Columbia, Maryland, 21046 ABSTRACT Savannah River Remediation (SRR) LLC is currently pursuing an aggressive program to empty its High Level Waste (HLW) tanks at the Savannah River Site (SRS). To accommodate this program, downstream processes, such as the Defense Waste Processing Facility (DWPF) and the Saltstone Production and Disposal Facilities, must improve overall throughput. To coincide with initiatives addressing improvements in salt processing, sludge processing enhancements have commenced which aim to improve the overall throughput in the DWPF. Specifically, three major enhancements have been proposed including the incorporation of an alternative reductant in the Chemical Process Cell (CPC), as well as two separate tasks addressing the reduction in water currently introduced during CPC processing. These enhancements promise to improve overall cycle time associated with melter feed preparation and reduce facility downtime. INTRODUCTION Commitments for bulk waste removal and subsequent waste tank closure at the Savannah River Site (SRS) require fundamental flowsheet changes to downstream processes to accommodate expeditious treatment and disposal of salt and sludge waste.
    [Show full text]
  • Energy-Efficient Glazing
    high-performance glass AIA CONTINUING EDUCATION energy-efficient glazing Y AUREGUIBERR J DE IER V A X Built after the original footbridge was destroyed in a 1996 bombing, this glass- and steel-enclosed bridge connects two buildings in Manchester, U.K. The hyperboloid shape required careful detailing of the seals between the glazing panels, to make them resist high wind loads and pressure changes. BY C.C. SULLIVAN AND ADAM SULLIVAN, LEARNING OBJECTIVES CONTRIBUTING EDITORS After reading this article, you should be able to: + DESCRIBE the basic process for producing float irtually all building types need windows and glazing to provide glass for use in architectural applications to enhance occupants with exterior views, natural daylight, and relief from visible light transmittance, solar management, and V a feeling of confinement. In recent years, a wide range of thermal performance in high-performance buildings. developments have renewed focus on glass technology itself. New + LIST several of the commonly used secondary formulations are changing the performance of glass in terms of visible glass treatment methods, such as heat treatment, light transmittance (VLT), solar management, and thermal perfor- lamination, coating, fritting, and tinting. mance. These advances make possible ever more efficient enclosures + DISCUSS how glazing manages solar energy, with ever greater glazed area. based on the properties of transmittance, emissivity, reflectance, and absorption. THE BASICS OF GLASS MANUFACTURING + COMPARE various strategies for glass retrofits, Developing an appropriate energy strategy for a project’s glazing including the use of building-integrated requires an understanding of the selected glass products’ technol- photovoltaics (BIPV). ogy and thermal-optical properties.
    [Show full text]
  • Frits and Sealing
    Frits and Sealing R. Morena Presented at Lehigh University as part of IMI-NFG Series on Glass Processing 14 April 2015 Lectures available at: www.lehigh.edu/imi Powdered glasses (frits) • Sealing Frits – • Coatings glaze (with opacifiers, colorants) glazes – ceramic porcelain enamel - ground coat + cover coat metal . Science & Technology © 2015 Corning Incorporated 2 . Starting point • Frits – finely powdered glasses that when re-heated will sinter, soften, and flow to form a seal or a coating (heat) At start: At finish: unconsolidated frit powder strong, hermetic seal or impervious coating . Science & Technology © 2015 Corning Incorporated 3 . Overview • Brief introduction, frits vs bulk glasses • Selection criteria for design of frit composition • Processing of frits . Science & Technology © 2015 Corning Incorporated 4 . Bulk glass vs frit behavior • By definition, glass is a thermodynamically unstable structure. • Converting a bulk glass to a fine powder only increases its instability. • Relatively few bulk glasses are stable as frits, but will crystallize to at least some extent BULK GLASS ? FRIT PROPERTIES PROPERTIES . Science & Technology © 2015 Corning Incorporated 5 . SnO-ZnO-P2O5 system Stable low temperature frits with good aqueous durability . Science & Technology © 2015 Corning Incorporated 6 . Classifications of frits • Vitreous – remains glassy throughout sealing cycle; will soften and flow if re-heated • Devitrifying – initially glassy, but at some point during sealing cycle will crystallize to form a hard, rigid bond. If reheated, will not flow and soften. • Typically, vitreous frits are desired where seals are subjected to repeat thermal cycling; devitrifying frits are preferred for applications in which the seal will be exposed to high operating temperatures . Science & Technology © 2015 Corning Incorporated 7 .
    [Show full text]
  • Chemical Hardening of Glazed Porcelain Tiles
    View metadata, citation and similar papers at core.ac.uk brought to you by CORE provided by Archivio istituzionale della ricerca - Università di Modena e Reggio Emilia DR SILVIA BARBI (Orcid ID : 0000-0001-5431-6906) MONIA MONTORSI (Orcid ID : 0000-0001-7217-7946) PROFESSOR CRISTINA SILIGARDI (Orcid ID : 0000-0003-1642-832X) Article type : Article Chemical hardening of glazed porcelain tiles Silvia Barbi1*, Consuelo Mugoni2, Monia Montorsi3, Cristina Siligardi2 1Interdepartmental Centre for applied research and services in advanced mechanics and motoring, University of Modena and Reggio Emilia, Modena, Italy; 2Department of Engineering “Enzo Ferrari”, University of Modena and Reggio Emilia, Modena, Italy; 3 Article Department of Sciences and Methods for Engineering, University of Modena and Reggio Emilia, Reggio Emilia, Italy; *[email protected] , +390592056281, via Vivarelli 10/1, 41125, Modena Abstract: Glazed ceramic tiles are used for wall and floor covering thanks to theirs high resistance to chemicals attacks, although big efforts should be done to increase their surfaces resistance to mechanical stresses. This study investigates the applicability of a well-known glass hardening process to glazed ceramic tiles following a rational design based on Design of Experiments technique. A Mixture Design has been carried out to formulate new frits compositions to enhance the ion exchange process, starting from a commercial product. Vickers Hardness and SEM-EDS techniques have been employed to evaluate the frits and elaborate the model. Results suggest that frits for ceramic tiles are positively affected by ion exchange process only if an appropriate combination of ions in the starting composition is present, establishing a new category of frit formulations suitable for that purpose.
    [Show full text]
  • Ferro Industrial Specialty Materials Glaze Catalog
    Technical Information GL18 Performance Colors and Glass Glaze Catalogue In this Technical Information bulletin we are Content introducing a selection of glazes for earthenware, tableware and art ceramics, stove tiles and Transparent glazes, lead free p. 2 stoneware. Transparent glazes, lead containing p. 4 Additionally, several useful specialty frits for glaze Matt glazes p. 5 corrections are listed. Opaque glazes p. 5 A catalogue with the most common glaze defects is Effect and oversaturation glazes p. 6 provided as well. Stoneware glazes p. 8 At the end of this bulletin, a table with the glaze Stove Tiles p 10 properties is given. Fashionable colors for superior designs p. 10 The here mentioned glazes and frits resemble only a Stylish design in up‐to‐date combinations p. 11 small selection of our complete product range. Conventional colors with a modern touch p.13 Please let us know if your desired glaze is not included. Up‐to‐date designs show the latest trends p. 14 For assistance in selecting and adapting your glazes, Traditional colors with modern appearance p. 18 please call our technical service department. Special frits p. 19 Glaze defects p. 20 Glaze properties p. 22 page 2/22 Transparent Glazes, Lead Free VTR 40 539 F transparent, glossy temperature range: 1040 to 1100 °C The glaze VTR 40 539 F is a universally suitable glaze for earthenware, tableware and art ceramics. It develops colors well, including pink stains (CaSnSiCr) and inclusion pigments, also with coloring oxides. Granulated glazes and stains can be stirred in. Interesting crystalline eliminations can be achieved with the addition of 248 030 (0.6 to 2.0 g for 100 g of glaze).
    [Show full text]
  • Archaeometric Characterization of 17Th Century Tin-Glazed Anabaptist
    1 Archaeometric characterization of 17th century tin-glazed Anabaptist (Hutterite) 2 faience artefacts from North-East-Hungary 3 4 Bernadett Bajnóczia1, Géza Nagya, Mária Tótha, István Ringerb, Anna Ridovicsc 5 6 aInstitute for Geological and Geochemical Research, Research Centre for Astronomy and 7 Earth Sciences, Hungarian Academy of Sciences, H-1112 Budaörsi út 45., Budapest, Hungary 8 bRákóczi Museum of the Hungarian National Museum, H-3950 Szent Erzsébet u. 19., 9 Sárospatak, Hungary 10 cHungarian National Museum, H-1088 Múzeum krt. 14-16., Budapest, Hungary 11 12 13 Abstract 14 The paper presents the first results of a long-term project aiming to reconstruct the production 15 technology of the Anabaptist (Hutterite) tin-glazed ceramics produced in Eastern-Central 16 Europe. Microanalytical investigations were performed on 17th-century faience artefacts (six 17 samples) excavated at Sárospatak, North-East-Hungary. The results are compared with 18 analytical data on the direct or indirect precursor, Italian maiolica. 19 The studied Hutterite faience artefacts reveal similarities with the Italian maiolica. 20 Calcareous clay with 14 to 22 wt% CaO was used for the buff-coloured ceramic body. Up to 21 about 400 µm thick, tin-opacified white and blue lead-alkali glaze was applied on the biscuit- 22 fired body. The glaze suspension contained sand admixture and a significant amount of 23 common salt and was not fritted before application. The colorants used for the ceramic 24 colours are lead antimonate for yellow, cobalt with arsenic, nickel and iron for blue, copper 25 for green and manganese with minor iron for black. The ceramic colours were applied on the 26 unfired glaze and maturing occurred during the second firing.
    [Show full text]