Arxiv:2103.16282V2 [Cond-Mat.Supr-Con] 28 May 2021 Form to Design High Superconducting Hydrides

Experimental observation of superconductivity at 215 K in calcium superhydride under high pressures

1, 2, 3, 1, 2, 1, 2, 1, 2 1, 2 Liang Ma, ∗ Kui Wang, ∗ Yu Xie, ∗ Xin Yang, Yingying Wang, Mi Zhou,2 Hanyu Liu,1, 2 Hongbo Wang,1, 2, † Guangtao Liu,2, ‡ and Yanming Ma1, 2, 3, § 1State Key Laboratory of Superhard Materials, College of Physics, Jilin University, Changchun 130012, China 2International Center of Computational Method & Software, College of Physics, Jilin University, Changchun 130012, China 3International Center of Future Science, Jilin University, Changchun 130012, China (Dated: May 31, 2021) The flourishing metal clathrate superhydrides are a class of recently discovered materials that possess record breaking near-room-temperature superconductivity at high pressures, because hydrogen atoms behave similarly to the atomic metallic hydrogen. While series of rare-earth clathrate superhydrides have been realized, the superconductivity of the first proposed clathrate calcium superhydride that initiates this major discovery has not been observed yet and remains of fundamental interest in the field of high-pressure physics. Here, we report the synthesis of calcium superhydrides from calcium and ammonia borane precursors with a maximum superconducting temperature of 215 K at 172 GPa, confirmed by the observation of zero resistance through four-probe electrical transport measurements. An exceedingly high upper critical magnetic field was estimated to be 203 T at zero temperature in the Werthamer–Helfand–Hohenberg model. Inferred from the synchrotron X-ray diffraction, together with the consistencies of superconducting transition temperature and equation of states between experiment and theory, sodalite-like clathrate CaH6 is one of the best candidates for this high-Tc CaHx.

PACS numbers:

The quest for room-temperature superconductors is one sized with observed Tc values ranging from 146 to 260 K that of the key issues in physics since the discovery of super- broke the superconductive record of 203 K in covalent H3S conductivity in 1911 [1, 2]. While atomic metallic hydro- [28], opening up a new era in search of room-temperature su- gen has been long considered as the most plausible candi- perconductors. date to achieve room-temperature superconductivity based on Although the prediction of CaH6 initiated the research wave Bardeen-Cooper-Schrieffer (BCS) theory [3–7], the realiza- of searching for high-temperature superconductors among tion of atomic metallic hydrogen is extremely challenging due clathrate metal superhydrides, only a handful of experiments to the requirement of unattainable synthetic pressures [8–10]. were conducted to explore Ca-H system at high pressures. Un- As substitutes, metallic hydrogen-rich materials, where hy- fortunately, while several calcium hydrides, such as Ca2H5 drogen is chemically pre-compressed in the lattice that might [29] and CaH4 [29, 30], have been synthesized from elemen- lower the stabilization pressure of metallic hydrogen, were tal Ca and H precursors, there was no any evidence for the ex- proposed to attain room-temperature superconductivity at ex- istence of CaH6. Consequently, the predicted high supercon- perimentally reachable pressures [11, 12]. Although much ductivity of clathrate calcium superhydrides was never con- efforts have been devoted to the exploration of compressed ﬁrmed. This not only hinders the understanding of the super- metallic hydrides [13–16], the theoretical and/or experimen- conducting and stabilization mechanisms for clathrate super- tal superconducting critical temperature (Tc) values in hy- hydrides but also hampers further design of clathrate super- drides were all below cuprates (164 K) until the report of hydrides with main-group metal skeleton. Thus, it is highly counterintuitive sodalite-like ionic clathrate CaH6 superhy- desired to probe the synthetic conditions for CaH6 and verify dride with a remarkably high Tc of 235 K at 150 GPa in 2012 the predicted superconductivity. Herein, we experimentally [17]. Importantly, the high superconductivity is originated performed a systematic structural and superconductive inves- from the clathrate hydrogen framework with strong electron- tigation of Ca-H system at various pressures and temperatures phonon interaction that closely mimics the physical proper- by combining laser-heated diamond-anvil cell (DAC) tech- ties of atomic metallic hydrogen, providing a general plat- niques, four-probe electromagnetic transport measurements, arXiv:2103.16282v2 [cond-mat.supr-con] 28 May 2021 form to design high superconducting hydrides. Following the and in situ synchrotron X-ray diffraction method. Elemental idea of CaH6, a class of ionic clathrate MH6 (M represents Ca and borane-ammonia (BH3NH3) were used as precursors metal elements) and two new clathrate superhydride proto- to synthesize calcium superhydride since BH3NH3 was found types MH9and MH10 have been later predicted for rare-earth to be a good candidate of hydrogen source at moderate pres- superhydrides with even higher Tc values above room temper- sure and temperature [21, 27, 31–35] that may prevent the for- ature [18–20]. Encouragingly, motivated by these theoretical mation of calcium hydrides with low hydrogen content. The predictions, a class of high-temperature superconductors, in- samples were heated to about 2000 K at pressures of 160-195 cluding YH6 [20, 21], YH9 [21, 22], CeH9, CeH10 [23], ThH9, GPa in the present work. Remarkably, the electrical trans- ThH10 [24], LaH10 [25, 26] and (LaY)H10 [27], were synthe- port measurements revealed a concrete superconducting tran- 2 (a) (b)

FIG. 1: The observation of superconductivity in CaHx. (a) Superconducting measurements in the calcium hydride CaHx. The resistances were measured with four electrodes on which the sample was placed (the upper left panel inset). Red curve, sample (cell_L1) heated at 181 GPa with Tc 207 K; blue curve, sample (cell_L2) heated at 170 GPa with Tc 212 K; green curve, sample (cell_L3) heated at 172 GPa with T 215∼ K. The resistance near the zero point is shown in a smaller scale∼ in the left bottom inset. (b) The dependence of the critical c ∼ temperature Tc on pressure; the eight different experiments are marked in different colors. Temperature dependence of the resistance at high pressures for the symbols of triangle and star are plotted in Fig. S1 and Fig. S2, respectively. sition of 215 K at 172 GPa. The consistencies of supercon- used to integrate powder diffraction rings and convert the 2- ducting transition temperature and equation of states between dimensional data to 1-dimensional profiles [37]. In XRD mea- experiment and theory evidence the highly possible synthesis surements, the pressure was determined by the equation of of clathrate CaH6 predicted earlier in Ref. [17]. state (EOS) of contacted Au electrode [38]. The resistances We synthesized calcium hydride via a reaction of calcium were measured via four-probe van der Pauw method with a (Alfa Aesar 99.5%) and BH3NH3 (Sigma-Aldrich, 97%). Ca current of 1-100 µA and four Au electrodes were placed on foil with the thickness of 2 µm was sandwiched between the the BH3NH3 plate. All magnetic measurements were carried BH3NH3. The diamonds used in DACs had culets with diame- out with nonmagnetic cells made of Be-Cu alloy. ter of 50-60 µm and were beveled at 8.5o to diameter of about The representative electrical resistance measurements as a 250 µm. Composite gasket consisting of a rhenium outer an- function of temperature at high pressures are shown in Fig. 1a. nulus and a cubic boron nitride (c-BN) epoxy mixture insert Superconducting transitions were evidenced by the sharply was employed to contain the sample while isolating the elec- drop of the resistance at 215, 212 and 207 K at about 172, trical leads in the electrical measurements. The sample prepa- 170 and 181 GPa, respectively. The observation of zero re- rations were done in an inert Ar atmosphere in a glovebox sistance (Inset in Fig. 1a) in some electrical experiments ex- with contents of O2 and H2O less than 0.01 ppm. The sample clude the possibility that the abruptly drop of resistance on was first isolated from the surrounding atmosphere by com- cooling arises from structural transition. In order to deter- pressing to about 20 GPa in the glove box and then taken out mine the highest value of Tc, we studied pressure dependence to further compression to the desirable pressure of 160-195 of Tc as shown in Fig. 1b. In different experimental runs, GPa. After loading, the sample was heated to about 2000 K Tc fluctuates slightly under the pressure of 170-186 GPa, and with a one-sided pulsed radiation from a YAG laser. The pres- then gradually decreases under higher pressures. The highest sure values in synthesis and electrical measurements were de- Tc of 215 K here observed in the sample is highly consistent termined from room-temperature diamond Raman measure- with our previously theoretical Tc (Coulomb pseudopotential ments [36]. µ* =0.13) of 220 K for Im-3m structured clathrate CaH6 [17]. In situ high-pressure angle-dispersive XRD experiments With decreasing pressure to about 130 GPa, the superconduct- at room temperature were performed principally at beamline ing transition vanishes as shown in Fig. S1, indicating a possi- BL15U1 (0.6199 Å) of the Shanghai Synchrotron Radiation ble decomposition of the superconducting state. The anomalous resistance peak at 200 K (red curve in Fig. 1a) which Facility. Some additional experiments were conducted at the ∼ 4W2 High Pressure Station of the Beijing Synchrotron Radi- was also observed in LaHx [25] might arise from the quantum ation Facility and BL10XU in SPring-8. The sample to detec- confinement and coherence effects of inhomogeneous super- tor distance and other geometric parameters were calibrated conductivity in the presence of disorder [39]. using a CeO2 standard. The software package Dioptas was Our typical size of calcium hydride samples is rather small 3

:172 GPa 200

:178 GPa

WHH 10

WHH 0.4 172 GPa

GL 180

WHH ) GL H (T) H 0

160 6

0 T WHH

140

2 3 T

120

206 208 210 212 214 216

GL 5 T Temperature (K)

H (T) H 100 0.2 0

GL 7 T 80

9 T 60 Resistance ( Resistance 40

:172 GPa

20 :178 GPa

0.0

160 180 200 220 0 50 100 150 200

Temperature (K) Temperature (K)

FIG. 2: Superconducting transitions of CaHx under external magnetic fields. Temperature dependence of the electrical resistance under applied magnetic fields of H = 0, 3, 5, 7, and 9 T at 172 GPa. Inset left: upper critical field Hc2 versus temperature following the criteria of 90% of the resistance in the metallic state at 172 GPa (red square, cell_M1) and 178 GPa (blue square, cell_M2), fitted with the GL and WHH models. Inset right: the dependence of the Tc under the applied magnetic field.

(20-25 µm in diameter), making it almost impossible to probe In order to further analyze the structures of the supercon- the weak signal of Meissner effect in the current experimen- ducting products, we prepared two DACs to carry out in-situ tal capabilities [22, 25]. Nevertheless, the superconducting XRD measurements at 173 (Fig. 3a and S4) and 181 GPa (Fig. nature of the transitions can be verified by its dependence on S5). Remarkably, the strong peak at around 14.5o observed in external magnetic fields. An applied external field could break two experiments coincides with the (100) diffraction of Im- the Cooper pairs due to the Pauli paramagnetic effect of elec- 3m structured CaH6. According to the theoretical XRD data o trons spin polarization and the diamagnetic effect of orbital of CaH6 at 170 GPa, besides the strong one at 14.54 , there o motion, thus reducing the Tc of material. As shown in Fig. should be another weak diffraction peak at 20.62 in the angle 2a, the resistance drop gradually shifts to lower temperatures range of measurements. Unfortunately, we did not observe as the magnetic field increased in the range 0-9 T at 172 GPa. this weak peak due to the relatively small scattering factor of Upper critical field as a function of temperature defined as Ca atom and the thin Ca foil precursor. We shall further per- 90% of the resistance as shown in inset of Fig. 2b. The appli- form synchrotron XRD measurements on the superconducting cation of a magnetic field reduces Tc by about 6 K at µ0H = 9 sample at a later base. Since we have the strong (110) peak T, confirming a superconducting transition. The extrapolation for CaH6 at hand, equation of state (EOS) of Im-3m structured values of the upper critical field µ0Hc2(T) and the coherence CaH6 from this peak is fitted in the unloading process and the length towards T = 0 K are 142 T and 15.2 Å and 203 T and result is highly consistent with the theoretical EOS as shown 12.7 Å (Fig. 2b) fitted by the Ginzburg–Landau (GL) [40] and Fig. 3b. It should be noted that the high-temperature super- Werthamer–Helfand–Hohenberg (WHH) [41] models, respec- conductivity of 213 K (inset in Fig. 3b) has also been observed tively. Another independent experiment at 178 GPa (Fig. S3) before synchrotron XRD study in latter cell. These evidences shows similar results that µ0Hc2(0) and the coherence length support that the best candidate for the high-temperature super- estimated with GL and WHH models are 132 T and 15.8 Å conductivity might be indeed the long-missing Im-3m struc- o and 181 T and 13.5 Å, respectively. The magnitude of the es- tured clathrate CaH6. Notably, other two peaks at 14.15 and timated coherence lengths ( 13-16 Å) is well below the typ- 14.95o can be indexed as (002) and (101) of CaH [29]. We ∼ 4 ical value (hundreds of angstrom) of type-I superconductors, should point out that there are still several unidentified peaks proving it is strongly type-II superconductor. indicated by asterisks, that may be from other unconsidered 4 (a) (b)

FIG. 3: Structural analysis. (a) Synchrotron X-ray diffraction pattern of superconducting calcium hydrides obtained following laser heating of Ca and BH3NH3 at 173 GPa. Unidentified reflections are indicated by asterisks. The diffraction peak marked by the black symbol is consistent with the (110) reflection of Im-3m CaH6. The diffraction peaks marked by the red symbols are consistent with the (002) and (101) reflections of I4/mmm CaH4. The diffraction peaks marked by the green symbols are fromc-BN decomposed from NH3BH3. (b) Experimental equation of state for the sample in this work in comparison with that of predicted Im-3m CaH6. The sample from cell_X1 was marked with red triangles, and the superconducting transition with Tc 213 K in the top inset was also measured at 181 GPa. The sample from cell_X2 was marked with blue inverted triangles. ∼ stoichiometry for current studies. (Fig. 3a). The high qual- search Program of Chinese Academy of Sciences (Grant No. ity XRD patterns are needed for further analysis in the future XDB33000000), and Program for JLU Science and Technol- study. In this work, we emphasize that the first experimen- ogy Innovative Research Team (JLUSTIRT). XRD measure- tal finding of high superconductivity with Tc above 200 K in ment were performed at Shanghai Synchrotron Radiation Fa- Ca-H system under high pressure. cility Beamline BL15U1, Beijing Synchrotron Radiation Fa- In summary, we synthesized CaHx at pressures of 160- cility HP-Station 4W2 and BL10XU/SPring-8. 195 GPa by laser heated DAC technique. The electromagnetic transport measurements reveal a superconducting transition of 215 K at 172 GPa that might arise from previously proposed long-missing Im-3m structured clathrate CaH6 [17]. L.M., K.W. and Y.X. equally contributed to this work. The present results provide the first experimental evidence for ∗ † Electronic address: [email protected] over 200 K high-temperature superconductivity in alkaline ‡ Electronic address: [email protected] earth superhydrides and might open up an era for searching § Electronic address: [email protected] room-temperature superconductors in non-rare earth ionic su- [1] H. Kamerlingh Onnes, The resistance of pure mercury at helium perhydrides. After completion of this work, we were aware of temperatures. Commun. Phys. Lab. Univ. Leiden, b 120 (1911). another independent experiment by Li et al. [42] where simi- [2] V.L. Ginzburg, Nobel Lecture: On superconductivity and super- lar results were also reported in calcium superhydride further fluidity (what I have and have not managed to do) as well as on the “physical minimum” at the beginning of the XXI century. proving the current work. Reviews of Modern Physics 76, 981 (2004). [3] N.W. Ashcroft, Metallic Hydrogen: A High-Temperature Su- We are grateful to Prof. Zhongxian Zhao for his kind sug- perconductor? Phys. Rev. Lett. 21, 1748 (1968). gestions and help in many aspects of this work. This work [4] E. Babaev, A. Sudbo, and N.W. Ashcroft, A superconductor to was supported by the Major Program of the National Natural superfluid phase transition in liquid metallic hydrogen. Nature Science Foundation of China (Grant No. 52090024), National 431, 666 (2004). [5] L. Zhang, Y. Niu, Q. Li, T. Cui, Y. Wang, Y. Ma, Z. He, and Key R&D Program of China (Grant no. 2018YFA0305900), G. Zou, Ab initio prediction of superconductivity in molecular National Natural Science Foundation of China (Grant No. metallic hydrogen under high pressure. Solid State Commun. 11874175, 12074139, 12074138, 11874176, 12034009 and 141, 610 (2007). 11974134), Jilin Province Outstanding Young Talents Project [6] P. Cudazzo, G. Profeta, A. Sanna, A. Floris, A. Continenza, (Grant No. 20190103040JH), the Strategic Priority Re- S. Massidda, and E.K. Gross, Ab initio description of high- 5

temperature superconductivity in dense molecular hydrogen. Troyan, and A.R. Oganov, Superconductivity at 161K in tho- Phys. Rev. Lett. 100, 257001(2008). rium hydride ThH10: Synthesis and properties. Materials Today [7] J.M. McMahon and D.M. Ceperley, High-temperature super- 33, 36 (2020). conductivity in atomic metallic hydrogen. Phys. Rev. B 84, [25] A.P. Drozdov, P.P. Kong, V.S. Minkov, S.P. Besedin, M.A. Ku- 144515 (2011). zovnikov, S. Mozaffari, L. Balicas, F.F. Balakirev, D.E. Graf, [8] M.I. Eremets, A.P. Drozdov, P.P. Kong, and H. Wang, V.B. Prakapenka, E. Greenberg, D.A. Knyazev, M. Tkacz, and Semimetallic molecular hydrogen at pressure above 350 GPa. M.I. Eremets, Superconductivity at 250 K in lanthanum hydride Nat. Phys. 15, 1246 (2019). under high pressures. Nature 569, 528 (2019). [9] P. Loubeyre, F. Occelli and P. Dumas, Synchrotron infrared [26] M. Somayazulu, M. Ahart, A.K. Mishra, Z.M. Geballe, M. Bal- spectroscopic evidence of the probable transition to metal hy- dini, Y. Meng, V.V. Struzhkin, and R.J. Hemley, Evidence for drogen. Nature 577, 631 (2020). Superconductivity above 260 K in Lanthanum Superhydride at [10] R.P. Dias and I.F. Silvera, Observation of the Wigner- Megabar Pressures. Phys. Rev. Lett. 122, 027001 (2019). Huntington transition to metallic hydrogen. Science 355, 715 [27] D.V. Semenok, I.A. Troyan, A.G. Kvashnin, A.G. Ivanova, (2017). M. Hanﬂand, A.V. Sadakov, O.A. Sobolevskiy, K.S. Per- [11] N.W. Ashcroft, Hydrogen dominant metallic alloys: high tem- vakov, A.G. Gavriliuk, and I.S. Lyubutin, Superconductivity at perature superconductors? Phys. Rev. Lett. 92, 187002 (2004). 253 K in lanthanum-yttrium ternary hydrides. arXiv preprint [12] J.J. Gilman, Lithium Dihydrogen Fluoride—An Approach to arXiv:2012.04787 (2020). Metallic Hydrogen. Phys. Rev. Lett. 26, 546 (1971). [28] A. P. Drozdov, M. I. Eremets, I. A. Troyan, V. Ksenofontov, [13] L. Zhang, Y. Wang, J. Lv, and Y. Ma, Materials discovery at and S. I. Shylin, Conventional superconductivity at 203 kelvin high pressures. Nat. Rev. Mater. 2, 1 (2017). at high pressures in the sulfur hydride system. Nature 525, 73 [14] H. Wang, X. Li, G. Gao, Y. Li, and Y. Ma, Hydrogen-rich su- (2015). perconductors at high pressures. WIREs Comput. Mol. Sci. 8, [29] A.K. Mishra, T. Muramatsu, H. Liu, Z.M. Geballe, M. So- e1330 (2018). mayazulu, M. Ahart, M. Baldini, Y. Meng, E. Zurek, and [15] J.A. Flores-Livas, L. Boeri, A. Sanna, G. Profeta, R. Arita, and R.J. Hemley, New Calcium Hydrides with Mixed Atomic and M. Eremets, A perspective on conventional high-temperature Molecular Hydrogen. J. Phys. Chem. C 122, 19370 (2018). superconductors at high pressure: Methods and materials. Phys. [30] G. Wu, X. Huang, H. Xie, X. Li, M. Liu, Y. Liang, Y. Huang, Rep. 856, 1 (2020). D. Duan, F. Li, B. Liu, and T. Cui, Unexpected calcium poly- [16] J. Lv, Y. Sun, H. Liu, and Y. Ma, Theory-orientated discovery of hydride CaH4: A possible route to dissociation of hydrogen high-temperature superconductors in superhydrides stabilized molecules. J. Chem. Phys. 150, 044507 (2019). under high pressure. Matter Radiat. Extrem. 5, 068101 (2020). [31] W. Chen, D.V. Semenok, A.G. Kvashnin, X. Huang, I.A. [17] H. Wang, J.S. Tse, K. Tanaka, T. Iitaka, and Y. Ma, Super- Kruglov, M. Galasso, H. Song, D. Duan, A.F. Goncharov, V.B. conductive sodalite-like clathrate calcium hydride at high pres- Prakapenka, A.R. Oganov, and T. Cui, Synthesis of molecular sures. Proc. Natl. Acad. Sci. U S A 109, 6463 (2012). metallic barium superhydride: pseudocubic BaH12. Nat. Com- [18] F. Peng, Y. Sun, C.J. Pickard, R.J. Needs, Q. Wu, and Y. Ma, mun. 12, 273 (2021). Hydrogen Clathrate Structures in Rare Earth Hydrides at High [32] D. Zhou, D.V. Semenok, H. Xie, X. Huang, D. Duan, A. Pressures: Possible Route to Room-Temperature Superconduc- Aperis, P.M. Oppeneer, M. Galasso, A.I. Kartsev, A.G. Kvash- tivity. Phys. Rev. Lett. 119, 107001 (2017). nin, A.R. Oganov, and T. Cui, High-Pressure Synthesis of Mag- [19] H. Liu, Naumov, II, R. Hoffmann, N.W. Ashcroft, and R.J. netic Neodymium Polyhydrides. J. Am. Chem. Soc. 142, 2803 Hemley, Potential high-Tc superconducting lanthanum and yt- (2020). trium hydrides at high pressure. Proc. Natl. Acad. Sci. U S A [33] D. Zhou, D.V. Semenok, D. Duan, H. Xie, W. Chen, X. Huang, 114, 6990 (2017). X. Li, B. Liu, A.R. Oganov, and T. Cui, Superconducting [20] I. A. Troyan, D. V. Semenok, A. G. Kvashnin, A.V. Sadakov, praseodymium superhydrides. Sci. adv. 6, eaax6849 (2020). O. A. Sobolevskiy, V. M. Pudalov, A. G. Ivanova, V. B. [34] T. Matsuoka, M. Hishida, K. Kuno, N. Hirao, Y. Ohishi, S. Prakapenka, E. Greenberg, A. G. Gavriliuk, I. S. Lyubutin, V. Sasaki, K. Takahama, and K. Shimizu, Superconductivity of V. Struzhkin, A. Bergara, I. Errea, R. Bianco, M. Calandra, F. platinum hydride. Phys. Rev. B, 99, 144511 (2019). Mauri, L. Monacelli, R. Akashi and A. R. Oganov, Anomalous [35] L. Ma, G. Liu, Y. Wang, M. Zhou, H. Liu, F. Peng, H. High-T emperature Superconductivity in YH6. Adv. Mater. 33, Wang, and Y. Ma, Experimental Syntheses of Sodalite-like 15 (2021). Clathrate EuH6 and EuH9 at Extreme Pressures. arXiv preprint [21] P. P. Kong, V. S. Minkov, M. A. Kuzovnikov, S. P. Besedin, arXiv:2002.09900, (2020). A. P. Drozdov, S. Mozaari, L. Balicas, F. F. Balakirev, V. B. [36] Y. Akahama and H. Kawamura, Pressure calibration of dia- Prakapenka, E. Greenberg, and M. I. Eremets, Superconductiv- mond anvil Raman gauge to 310 GPa. J. Appl. Phys. 100, ity up to 243 K in yttrium hydrides underhigh pressure. arXiv 043516 (2006). preprint arXiv:1909.10482 (2019). [37] C. Prescher and V.B. Prakapenka, DIOPTAS: a program for re- [22] E.Snider, N. Dasenbrock-Gammon, R. McBride, X. Wang, duction of two-dimensional X-ray diffraction data and data ex- N. Meyers, K. V. Lawler, E. Zurek, A. Salamat, and R. P . ploration. High Pressure Res. 35, 223 (2015). Dias, Synthesis of Yttrium Superhydride Superconductor with [38] K. Jin, Q. Wu, H. Geng, X. Li, L. Cai, and X. Zhou, Pressure– a Transition Temperature up to 262 K by Catalytic Hydrogena- volume–temperature equations of state of Au and Pt up to 300 tion at High Pressures. Phys. Rev. Lett. 126, 1117003 (2021). GPa and 3000 K: internally consistent pressure scales. High [23] W. Chen, D. V. Semenok, X. Huang, H. Shu, X. Li, D. Duan, Pressure Res. 31, 560 (2011). T. Cui, and A. R. Oganov, High-Temperature Superconductiv- [39] G. Zhang, T. Samuely, J. Kacmarˇ cík,ˇ E.A. Ekimov, J. Li, J. ity in Cerium Superhydrides. arXiv preprint arXiv: 2101.01315 Vanacken, P. Szabó, J. Huang, P.J. Pereira, D. Cerbu and V.V. (2021). Moshchalkov, Bosonic Anomalies in Boron-Doped Polycrys- [24] D.V. Semenok, A.G. Kvashnin, A.G. Ivanova, V. Svitlyk, V.Y. talline Diamond. Phys. Rev. Appl. 6, 064011 (2016). Fominski, A.V. Sadakov, O.A. Sobolevskiy, V.M. Pudalov, I.A. [40] V.L. Ginzburg and L.D. Landau, On the Theory of supercon- 6

ductivity. Zh.Eksp.Teor.Fiz. 22, 1064 (1950). [42] Z.W. Li, X. He, C.L. Zhang, S.J. Zhang, S. M. Feng, [41] N.R. Werthamer, E. Helfand, and P.C. Hohenberg, Temperature X.C. Wang, R.C. Yu, and C.Q.Jin, Superconductivity above and Purity Dependence of the Superconducting Critical Field, 200K Observed in Superhydrides of Calcium, arXiv preprint Hc2. III. Electron Spin and Spin-Orbit Effects. Phys. Rev. 147, arXiv:2103.16917, (2021). 295 (1966). Supplementary Material for “Experimental observation of superconductivity at 215 K in calcium superhydride under high pressures”

Liang Ma,1,2,3,? Kui Wang,1,2,? Yu Xie,1,2,? Xin Yang,1,2 Yingying Wang,1,2 Mi 2 1,2 1,2, 2, 1,2,3, Zhou, Hanyu Liu, Hongbo Wang, †, Guangtao Liu, ‡ and Yanming Ma § 1State Key Laboratory of Superhard Materials, College of Physics, Jilin University, Changchun 130012, China 2International Center of Computational Method & Software, College of Physics, Jilin University, Changchun 130012, China 3International Center of Future Science, Jilin University, Changchun 130012, China †Electronic Address: [email protected] ‡Electronic Address: [email protected] §Electronic Address: [email protected] ? L.M., K.W. and Y .X. equally contributed to this work (Dated: May 31, 2021)

Fig. S1. The sample was synthesized at around 170 GPa from a mixture of Ca and BH3NH3 (cell L4). Supercon- ducting steps shown by the temperature dependence of the resistance at diﬀerent pressures. The pressure dependence of the onset of superconductivity is shown in the inset: Tc shifts to lower temperatures as the pressure is decreased. arXiv:2103.16282v2 [cond-mat.supr-con] 28 May 2021 2

FIG. S2. The sample was synthesized at around 160 GPa from a mixture of Ca and BH3NH3 (cell L5). Supercon- ducting steps shown by the temperature dependence of the resistance at diﬀerent pressures The pressure dependence of the onset of superconductivity is shown in the inset: Tc shifts to lower temperatures as the pressure is decreased.

FIG. S3. Superconducting transitions in the CaHx (cell M2). (a) dependence of the electrical resistance and critical temperature of CaHx on the external magnetic ﬁelds (0, 3, 5, 7, 9 T) at 178 GPa; (a) dependence of the electrical resistance and critical temperature of CaHx on the external magnetic ﬁelds (1, 2, 4, 6, 8 T) at 178 GPa. 3

FIG. S4. Experimental XRD patterns during decompression in the pressure range of 173–125 GPa.

FIG. S5. Experimental XRD patterns during decompression in the pressure range of 181–131 GPa. 4

FIG. S6. The typical photograph (a) before and (b)after heating. After laser heating, the heated part of sample turned black.

FIG. S7. Temperature dependence of the resistance in the warming cycle at around 160 GPa before laser heating. The superconductivities originated from element Ca.