095/1 Effects of Pouring Temperature and Squeeze Pressure on The

Total Page:16

File Type:pdf, Size:1020Kb

095/1 Effects of Pouring Temperature and Squeeze Pressure on The Effects of Pouring Temperature and Squeeze Pressure on the Properties of Al-8%Si Alloy Squeeze Cast Components A. Raji* & R. H. Khan** *Department of Mechanical Engineering, Federal University of Technology, Yola, Adamawa State, Nigeria. **Department of Mechanical Engineering, Federal University of Technology, P.M.B. 65, Minna, Niger State, Nigeria. Abstract This work was conducted to determine the optimum squeeze parameters for producing squeeze castings from the Al alloy and compare the properties of the squeeze castings with those of chill castings. Al alloy Squeeze castings were produced using squeeze pressures of 25-150MPa at steps of 25MPa with the alloy poured at 650oC, 700oC and 750oC for each of the indicated pressure into a die preheated to about 250oC. Squeeze time was maintained for 30 seconds. It was found that for a specific pouring temperature, the grain size of squeeze cast products became finer; density and the mechanical properties were increased with increase in squeeze pressure to their maximum values while further increase in pressure did not yield any meaningful change in the properties. Squeeze cast sample properties were compared with those of chill cast samples. It was found that optimum pouring temperature of 700oC and squeeze pressure of 125MPa could be used to produce sound squeeze cast Al alloy components with aspect ratio (height-to-section thickness ratio) not greater than 2.5:1. Keywords: Squeeze casting, Aluminium alloy, Pouring temperature, Squeeze pressure, Mechanical properties. 095/1 Introduction Squeeze casting, compared with traditional sand casting which dates back to about 2000-3500B.C. It is a relatively new casting technology [1,2]. It is a technology with very bright future, based on its applications and advantages. Yue and Chadwick [3] described squeeze casting as a casting process in which molten metal is solidified under the direct action of a pressure that is sufficient to prevent the appearance of either gas porosity or shrinkage porosity as opposed to all other casting processes in which some residual porosity is left. They further observed that the process is also known, variously as liquid-metal forging, squeeze forming, extrusion casting and pressure crystallisation. Squeeze casting has a number of advantages which have been discussed by various researchers [4-8]. Some of the advantages include elimination of gas and shrinkage porosities, reduction or elimination of metal wastage due to absence of feeders or risers; ability to cast both cast and wrought alloys; possibility of manipulation of process parameters to achieve the required optimum parameters. Squeeze casting is a very important manufacturing process, which combine the advantages of forging and casting used for the production of many range of products from monolithic alloys and metal-matrix composites parts. Such parts include vane, ring groove reinforced piston, connecting rod, M6-8 bolt, joint of aerospace structure, rotary compressor vane, shock absorber cylinder, diesel engine piston, cylinder liner bearing materials among many others used in automobile, nuclear, aeronautical components, sports equipment and many industrial equipment [9,10]. Despite its relatively small age, squeeze casting has witnessed a lot of development in the sphere of products and materials cast and quite a number of research studies have been carried out to improve the process particularly in the areas of molten metal metering and metal movement system during pouring into the die, lubrication systems and the use of reinforcement among others. However, in spite of all these researches, it was observed that squeeze casting particularly the relationship between the design, the process parameters and the quality of the squeeze cast components was yet to be fully understood; thus the need for more studies in this area of technology for better understanding of the process [11]. This study was carried out to determine the effect of squeeze pressure and pouring temperature on aluminium-silicon alloy squeeze cast products with aspect ratio (height-to-section thickness ratio) up to 2.5:1. Materials and Methods In this study, an Al alloy, the composition of which is given below and lubricant consisting of 10% graphite in lubricating oil of the type 20W/50 were used: Si-8.08%, Cu-1.920%, Fe-.0.686%, Mn-0.173%, Ni-0.086%, Al- Rem. 095/2 Melting was carried out in a resistance furnace & a 150t hydraulic press was used for squeezing operation. Series of experiments involving casting of the shape shown in Fig.1 were carried out using squeeze casting, sand casting and chill casting methods. Specimens were then prepared from the castings with the aim of determining the mechanical properties and microstructure of castings by the various techniques and the results were compared with each other. MELTING OF THE ALLOY Melting was carried out in an electric resistance furnace. The alloy was charged into a preheated crucible. Covering flux, 2% by weight of charge was used to prevent from oxidation & gas pick up. Degassing was carried out using hexachloroethane tablets (0.5% of melt) before pouring at the desired temperatures of 650, 700 or 750 degree centigrade. Temperature was measured using immersion pyrometer. CHILL CASTING A two part permanent mould made from mild steel was employed for making chill castings (at atmospheric pressure and squeeze pressure of 0MPa). The lower half of the permanent mould was mounted on the hydraulic press and its internal surface was preheated to a temperature of 160oC. Simultaneously, the upper part of the mould was placed upside down and the surface was similarly preheated. The surfaces of the mould that were to be in contact with the molten metal were coated with a prepared lubricant (graphite in lubricating oil). The two parts of the mould were preheated to a temperature of 250oC. The two parts were then assembled together. Molten aluminium-silicon alloy of the required temperature was then poured from the crucible into the assembled mould. The metal was allowed to stand for a period of 5mins after which the moulds were separated and the casting ejected out of the mould. Three sets of three chill castings were made with the alloy poured at 650oC, 700oC and 750oC. SQUEEZE CASTING Squeeze castings were made using a two- part die, the lower die and the upper die (punch), made from mild steel. The lower die was mounted on a supporting bed of the hydraulic press table. The punch was attached to the ram of the hydraulic press. The assembly was enclosed in a casing to isolate it from the shop atmosphere. With the door of the casing opened, the die heater was placed in between the two halves of the die. Thereafter, the door was closed. The probe for the immersion pyrometer was then placed in the 8mmØ hole located in the lower half of the die through an opening in the door. The die surface heater was switched on to preheat the lower and upper dies. When the temperature of the Squeeze casting die reached 160oC, the door was opened, the punch was raised and the heater was withdrawn from the die. A prepared lubricant made up of 10% of graphite in lubricating oil was applied on the surfaces of the die that were to be in contact with the molten metal. The heater was replaced in its 095/3 position, the punch was lowered, the door was closed and the dies were then preheated to the temperature of 240-250oC). Thereafter, the door of the casing was opened; the punch was withdrawn upward to a position from which it could readily strike. The heater was once more removed away. Measured quantity of the aluminium alloy at the required pouring temperature was poured into the lower die. The punch was then brought down with a velocity of 9.45mm/s onto the lower die and the required pressure was applied for a period of 30s. The punch was, thereafter, withdrawn upward. The solidified casting was ejected from the lower die with the help of ejector pins. Squeeze castings were made using 25, 50, 75, 100, 125 and 150MPa with the alloy poured at 650oC, 700oC and 750oC for each of the indicated pressure. Three sets of squeeze castings were made for each combination of squeeze pressure and pouring temperature. Metallographic examination, density, hardness and tensile properties were evaluated for the samples cast. Results and Discussion The results of density, hardness and strength characteristics are shown in Figs.2-6. Properties at squeeze pressure of 0MPa refer to those of chill castings. DENSITY The relationship between density of the Al alloy chill castings as well as squeeze castings and squeeze pressure for various pouring temperature is depicted in Fig. 2. The density of the chill castings and squeeze castings varied from 2.712 for chill castings to 2.866 g/cm3 for squeeze castings that is about 5.68% increase compared to chill castings. In all pouring temperatures, the density increased with increase in squeeze pressure. There was a very steep increase in the density from 2.718 at squeeze pressure of 0MPa to 2.820 g/cm3 at squeeze pressure of 75MPa for the pouring temperature of 650oC and thereafter it increased gently (almost horizontally) to 2.830g/cm3 at 150MPa. Similarly, for the pouring temperature of 700oC, the density increased steeply from 2.720 at 0MPa to 2.842g/cm3 at 75MPa and thereafter it increased gently to 2.863g/cm3 at 150MPa. For the pouring temperature of 750oC, the density increased from 2.712 at 0MPa to 2.778g/cm3 at 50MPa and 2.857g/cm3 at 75MPa. Thereafter it increased slightly to 2.866g/cm3 at 150MPa. Hence, the curves for 700oC and 750oC tend towards each other. The trend could be attributed to the fact that squeeze pressure tends to decrease gas porosities and decrease the inter-atomic distances and as these gas porosities and distances decrease the castings become more compact.
Recommended publications
  • Troubleshooting Decorative Electroplating Installations, Part 5
    Troubleshooting Decorative Electroplating Installations, Part 5: Plating Problems Caused Article By Heat & Bath Temperature Fluctuations by N.V. Mandich, CEF, AESF Fellow Technical Technical In previous parts of this series, emphasis was given The fast-machining steels must then be carburized to troubleshooting of the sequences for pre-plating or case-hardened to obtain a surface with the hardness and electroplating over metals, Parts 1 and 2;1 required to support the top chromium electroplate. the causes, symptoms and troubleshooting for Case hardening is the generic term covering several pores, pits, stains, blistering and “spotting-out” processes applicable to steel or ferrous alloys. It changes phenomena, Part 3;2 and troubleshooting plating on the surface composition of the top layer, or case, by plastic systems, Part 4.3 Here in Part 5, causes and adsorption of carbon, nitrogen or a mixture of the two. some typical examples of problems that occur in By diffusion, a concentration gradient is created. The electroplating as a result of a) thermal, mechanical heat-treatments and the composition of the steel are surface treatments, b) the metallurgy of the part to additional variables that should be addressed and taken be plated or c) effects of plating bath temperature into account in the electroplating procedure. on plating variables and quality of the deposits When discussing the effect of heat-treatment on are discussed. subsequent electroplating processes it is necessary to zero in on the type of heat-treatment involved. We Nearly every plater has at one time or another had the can defi ne the heat-treatment process as changing the experience of trying to plate parts that simply would characteristics of the parts by heating above a certain not plate.
    [Show full text]
  • Electroforming of Copper Canisters
    Mineralogical Magazine, November 2015, Vol. 79(6), pp. 1521–1528 OPEN ACCESS Manufacturing technology for implementing geological disposal: electroforming of copper canisters 1,2,3,* 1,3 1,4 2 2 T. H ERNANDEZ-SELVA ,D.L.ENGELBERG ,F.SCENINI ,D.FOX AND A. MCCLUSKY 1 Materials Performance Centre, School of Materials, The University of Manchester, Manchester M13 9PL, UK 2 BEP Surface Technologies Ltd, Eton Hill Road, Radcliffe, Manchester M26 2XT, UK 3 Research Centre for Radwaste and Decommissioning, The University of Manchester, Manchester M13 9PL, UK 4 Nuclear Advanced Manufacturing Centre, The University of Manchester, Manchester M13 9PL, UK ABSTRACT The existing capability and current development needs for implementing electroforming as a viable manufacturing process to produce copper cylinders with dimensions comparable to the Swedish KBS-3 design are discussed. Large freestanding copper cylinders can be produced readily, but there is a need to address challenges associated with controlling the electro-deposition process to conform to compositional and mechanical requirements of the copper layers produced. The methodology to optimize the manufacturing process, based on a study of key parameters, such as the effects of electrolyte additives on grain size and the chemical composition of electroformed layers, is described here. Possible ways to introduce a robust manufacturing route are also presented. K EYWORDS: nuclear wastes, deep geological repository, KBS-3 copper canister, electroforming, electroplating. Introduction Institute, 2006; ARAO, 2009), whereas the Nuclear Waste Management Organization (NWMO) of THE concept for the UK’s inventory of high-level Canada is focusing its research on thick-walled radioactive waste (HLW) is to implement deep steel containers coated with 3 mm of electroplated geological disposal (Department of Energy & copper (Keech et al., 2014).
    [Show full text]
  • Enhanced Fracture Strength in the Working Layer of Rolls Manufactured in Ni-Hard Cast Iron Alloyed with Mo, Nb and Mg
    metals Article Enhanced Fracture Strength in the Working Layer of Rolls Manufactured in Ni-Hard Cast Iron Alloyed with Mo, Nb and Mg Alberto Cofiño-Villar 1, Jose Florentino Alvarez-Antolin 1,* and Juan Asensio-Lozano 2 1 Departamento de Ciencia de los Materiales e Ingeniería Metalúrgica, Edificio departamental Este, Universidad de Oviedo C/ Wifredo Ricart s/n-, 33204 Gijón (Asturias), Spain; [email protected] 2 Departamento de Ciencia de los Materiales e Ingeniería Metalúrgica, Escuela de Ingeniería de Minas, Energía y Materiales, Universidad de Oviedo, C/ Independencia 13, 33004 Oviedo (Asturias), Spain; [email protected] * Correspondence: alvarezfl[email protected]; Tel.: +34-985-181-949 Received: 28 August 2018; Accepted: 13 September 2018; Published: 15 September 2018 Abstract: One of the main in-service failure mechanisms of the work-rolls used in hot strip mill finishing stands is surface spalling. The indefinite chill double-poured rolls usually comprise of a peripheral working layer made of crushed Ni-hard cast iron and a grey cast iron core, mostly pearlitic matrix with spheroidal graphite. To enhance its wear resistance, the working layer can be alloyed with Mo and Nb. The possible cracking and spalling of the surfaces of these work-rolls is strongly influenced by the presence of carbides and the continuity of their network. The flexural and impact toughness tests are reliable testing methods to assess these properties. The aim of this paper is to identify those manufacturing factors that have a significant effect on the flexural strength and toughness of this material, correlating the results with the volume fraction of precipitated carbides.
    [Show full text]
  • ZEP LUBEZE DRILL CHILL™ Cutting Oil
    PROD. #1378 205 PRODUCT SPECIFICATION REPORT ZEP LUBEZE DRILL CHILL™ Cutting Oil DESCRIPTION A fatty, mineral oil based, ready to use metalworking fluid, fortified with extremely pressure additives. FEATURES BENEFITS • Versatile • Can be used on carbon, allot, and stainless steel as well as softer metals such as aluminum. • Anti weld • Helps prevent chips from welding to tool surface • Prolongs tool life • Reduces friction, increases cutting speeds • Inhibits rust • Leaves behind a light oil film which provides temporary protection to the work piece and tool surface • Conserves energy • Lowers resistance to cutting resulting in lower torque and power requirements APPLICATIONS An excellent lubricating fluid for metalworking applications, particularly in extreme pressure situations such as drilling and threading. Used in any metalworking and fabricating facility. COMPANION PRODUCTS Zep Gator Tails, Zep degreasers, Zep Cold Galvanized, Zep Super Penetrant, Zep Ironclad, Zep PLS, Zep Viton Gloves SPECIFICATIONS Physical form . .Thin, amber oil Boiling point . .545 - 884°F Flash point (TCC) . .300°F Shelf life . .1 year minimum Odor . .solvent odor DOT Shipping label . .LUBRICANTS, METAL CUTTING, pH . .N/A . .LIQUID, NOI Specific gravity . .0.88 PACKAGING 5 gallon pail 55 gallon drum ZEP MANUFACTURING COMPANY 1-877-I BUY ZEP Your One Source for Cleaning and Maintenance Products (1-877-428-9937) PROD. #1378 205 PRODUCT LABEL ZEP LUBEZE DRILL CHILL™ Cutting Oil ™ PROD.# 1378 LUBEZE DRILL CHILL 501B CUTTING OIL •Drilling •Cutting •Boring •Thread Cutting and Machining Operations A premium cutting oil fortified with sulfur and chlorine compounds for FIRST AID: effectiveness in extreme pressure applications. Provides excellent lubricity. EYES: Immediately flush eyes with plenty of water for at least 15 minutes, occasionally Reduces energy requirements by lowering resistance to cutting tool.
    [Show full text]
  • From the on Inal Document. What Can I Write About?
    DOCUMENT RESUME ED 470 655 CS 511 615 TITLE What Can I Write about? 7,000 Topics for High School Students. Second Edition, Revised and Updated. INSTITUTION National Council of Teachers of English, Urbana, IL. ISBN ISBN-0-8141-5654-1 PUB DATE 2002-00-00 NOTE 153p.; Based on the original edition by David Powell (ED 204 814). AVAILABLE FROM National Council of Teachers of English, 1111 W. Kenyon Road, Urbana, IL 61801-1096 (Stock no. 56541-1659: $17.95, members; $23.95, nonmembers). Tel: 800-369-6283 (Toll Free); Web site: http://www.ncte.org. PUB TYPE Books (010) Guides Classroom Learner (051) Guides Classroom Teacher (052) EDRS PRICE EDRS Price MF01/PC07 Plus Postage. DESCRIPTORS High Schools; *Writing (Composition); Writing Assignments; *Writing Instruction; *Writing Strategies IDENTIFIERS Genre Approach; *Writing Topics ABSTRACT Substantially updated for today's world, this second edition offers chapters on 12 different categories of writing, each of which is briefly introduced with a definition, notes on appropriate writing strategies, and suggestions for using the book to locate topics. Types of writing covered include description, comparison/contrast, process, narrative, classification/division, cause-and-effect writing, exposition, argumentation, definition, research-and-report writing, creative writing, and critical writing. Ideas in the book range from the profound to the everyday to the topical--e.g., describe a terrible beauty; write a narrative about the ultimate eccentric; classify kinds of body alterations. With hundreds of new topics, the book is intended to be a resource for teachers and students alike. (NKA) Reproductions supplied by EDRS are the best that can be made from the on inal document.
    [Show full text]
  • Metal Casting Terms and Definitions
    Metal Casting Terms and Definitions Table of Contents A .................................................................................................................................................................... 2 B .................................................................................................................................................................... 2 C .................................................................................................................................................................... 2 D .................................................................................................................................................................... 4 E .................................................................................................................................................................... 5 F ..................................................................................................................................................................... 5 G .................................................................................................................................................................... 5 H .................................................................................................................................................................... 6 I ....................................................................................................................................................................
    [Show full text]
  • Performance Evaluation of Different Materials As Chills in Sand Casting of Aluminium Alloy
    PERFORMANCE EVALUATION OF DIFFERENT MATERIALS AS CHILLS IN SAND CASTING OF ALUMINIUM ALLOY BY KABIRU MUFTAU RAJI M.Sc/ENG/ 08222/2010-2011 A DISSERTATION SUBMITTED TO THE SCHOOL OF POSTGRADUATE STUDIES, AHMADU BELLO UNIVERSITY ZARIA, KADUNA STATE, NIGERIA IN PARTIAL FULFILLMENT OF THE REQUIREMENTS FOR THE AWARD OF A MASTER DEGREE IN MECHANICAL ENGINEERING DEPARTMENT OF MECHANICAL ENGINEERING, FACULTY OF ENGINEERING AHMADU BELLO UNIVERSITY, ZARIA, NIGERIA. FEBRUARY, 2016 i DECLARATION I declare that the work in this Dissertation entitled Performance Evaluation of Different Metallic Materials as Chills in Sand Casting of Aluminium Alloy has been carried out by me in the Department of Mechanical Engineering, Ahmadu Bello University, Zaria. The information derived from the literature has been duly acknowledged in the text and a list of references provided. No part of this thesis was previously presented for another degree or diploma at this or any other institution. Kabiru Muftau Raji ……..………………… ……...……………. Name of Student Signature Date ii CERTIFICATION This dessertation entitled Performance Evaluation of Different Materials as Chills in Sand Casting of Aluminium Alloy by Kabiru Muftau RAJI meets the regulations governing the award of the degree of Master in Mechanical Engineering of the Ahmadu Bello University, and is approved for its contribution to knowledge and literacy presentation. Dr. D.S. Yawas ……………………. ………………… Chairman, Supervisory Committee Signature Date Prof. A. I. Obi …………………… ………………… Member, Supervisory Committee Signature Date Dr. M. I. Dauda ……………………. ………………... Head of Department Signature Date Prof. kabir Bala …………………… ………………… Dean, School of Postgraduate Studies Signature Date iii DEDICATION This dissertation is dedicated to the Almighty GOD, the Most Beneficent and the Most Merciful.
    [Show full text]
  • Improvement of Casting Speed and Billet Quality of Direct Chill Cast Aluminum Wrought Alloy with Combination of Slit Mold and Electromagnetic Coil
    Materials Transactions, Vol. 48, No. 8 (2007) pp. 2194 to 2201 #2007 The Japan Institute of Metals Improvement of Casting Speed and Billet Quality of Direct Chill Cast Aluminum Wrought Alloy with Combination of Slit Mold and Electromagnetic Coil Hai Hao, Xingguo Zhang, Shan Yao and Junze Jin State Key Laboratory of Materials Surface Modification by Laser, Ion and Electronic beams, School of Materials Science and Engineering, Dalian University of Technology, Dalian, 116023, P.R. China A mold with slits and external cooling water channels was designed for the direct chill casting processing. By imposing a high frequency magnetic field, the surface quality and microstructure of the direct chill cast billets are improved. The casting speed could be improved by the simultaneous use of mold and electromagnetic coil. In the case of one kind of Al-Cu-Mg alloy with a wide freezing range, the critical casting speed to break-out can be improved 60%. The microstructure of the billet cast with electromagnetic field is more fine and uniform than that of the conventionally cast billet, and the subsurface segregation usually observed in the conventional billets is eliminated. [doi:10.2320/matertrans.MRA2007030] (Received February 5, 2007; Accepted May 14, 2007; Published July 11, 2007) Keywords: direct chill casting, aluminum wrought alloy, electromagnetic casting, casting speed 1. Introduction front is limited in the certain zone of the inductor acting. A novel technique is described in this paper, which combines As the premier process for producing aluminum shapes the DC mold and the electromagnetic coil and leads to high suitable for subsequent processing in extrusion, rolling or quality aluminum billet with smooth surface, fine structure, remelt operations, the direct chill casting (DCC) technolog- especially, under an improving casting speed.
    [Show full text]
  • Hot Tearing and Deformation in Direct-Chill Casting of Aluminum Alloys
    Hot tearing and deformation in direct-chill casting of aluminum alloys Suyitno Hot tearing and deformation in direct-chill casting of aluminum alloys Proefschrift ter verkrijging van de graad van doctor aan de Technische Universiteit Delft, op gezag van de Rector Magnificus Prof. dr. ir. J.T. Fokkema, voorzitter van het College voor Promoties, in het openbaar te verdedigen op maandag 30 mei 2005 te 10.30 uur door Suyitno bachelor of engineering in werktuigbouwkunde master of science in materialkunde geboren te Semarang, Indonesia Dit proefschrift is goedgekeurd door de promotor: Prof. ir. L. Katgerman Toegevoed promotor: Dr. W.H. Kool Samenstelling promotiecommissie: Rector Magnificus, voorzitter Prof. ir. L. Katgerman, Technische Universiteit Delft, promotor Dr. W.H. Kool, Technische Universiteit Delft, toegevoed promotor Prof. dr. R. Boom, Technische Universiteit Delft & CORUS Prof. dr. I.M. Richardson, Technische Universiteit Delft Prof. dr. ir. S. van der Zwaag, Technische Universiteit Delft Prof. dr. A. Mo, SINTEF Materials Technology, Oslo, Norway Dr. ir. R.N. Kieft, CORUS RD&T, Ijmuiden This research was carried out as part of the strategic research program of the Netherlands Institute for Metals Research (NIMR) on the “Experimental description and process simulation of direct-chill (DC) casting of aluminum alloys” project number MP 97014. ISBN 90-9019393-6 Copy right © 2005 by Suyitno All right reserved. No part of the material protected by this copy right notice may be reproduced or utilized in any form or by any means, electronical or mechanical, including photocopying, recording or by any information storage and retrieval system, without written permission from the author.
    [Show full text]
  • Construction Materials Engineering
    TOMSK POLYTECHNIС UNIVERSITY I.A. Khvorova CONSTRUCTION MATERIALS ENGINEERING PRACTICE It is recommended for publishing as a study aid by the Editorial Board of Tomsk Polytechnic University Tomsk Polytechnic University Publishing House 2015 Created with novaPDF Printer (www.novaPDF.com). Please register to remove this message. UDC 669.018.29=11(076.8) BBC 30.3=432.11я73 K42 Khvorova I.А. K42 Construction Materials Engineering. Practice / I.А. Khvorova, Y.A. Evtushkin, N.I. Fomin, V.N. Obrastcov; Tomsk Polytechnic Uni- versity. − Tomsk: TPU Publishing House, 2015. – 66 p. The study aid contains methodical instructions for laboratory works on discipline “Construction Materials Engineering” and is intended for training students majoring in the direc- tion 150700 “Mechanical engineering” in English. The laboratory practice is directed to inten- sification of theoretical knowledge in discipline and allows students to get practical skills in processing of materials. UDC 669.018.29=11(076.8) BBC 30.3=432.11я73 © STE HPT TPU, 2015 © Khvorova I.A., 2015 © Design. Tomsk Polytechnic University Publishing House, 2015 2 Created with novaPDF Printer (www.novaPDF.com). Please register to remove this message. LABORATORY WORK № 1 MANUFACTURING OF EXPENDABLE CASTING MOULD Laboratory work objective 1. Study properties and mixing ratio of sand mix and core sand mixture. 2. Study equipment, tools and devices applied for molding. 3. Study technological process of a casting mould manufacturing. 4. Make a casting mould under the supervision of the instructor. The equipment and materials 1. Molding plate. 2. Bin with sand mix. 3. Casting pattern. 4. Flasks (molding boxes). 5. Core box.
    [Show full text]
  • Aging: Changing the Physical Properties of a Metal to Improve Its Hardness and Strength
    Aging: Changing the physical properties of a metal to improve its hardness and strength. Alloy: Two or more elements combining, at least one of which is metal, to change the properties of the material and potentially lower its cost. Annealing: A process that softens metals via heat treating above the critical temperature and slow cooling to reduce hardness and improve ma- chinability. Airset Core: Using sand mixture with two-part resin, hand packed into a core box to form a sand core. As-Cast: No heat treat or finishing condition. Bath: Molten metal in a crucible or ladle. Binder: Agent used to bind mold or core sand to improve strength. Blast Cleaning: Metal shot used to clean or remove sand from castings Brinell Hardness: Testing method for hardness of a material using a specific ball diameter and applying a load (BHN). Burn-on Sand: Sand that has adhered to a cast surface that is hard to remove. Castability: How well a metal flows through the mold to create an accurate casting. Chaplet: A metal insert used to support a core during casting. Charge: Material placed into a furnace. Chill: Metal insert in a sand mold that causes heat loss to control solidification of a casting. Cleaning: Removing gates, risers, flash, and parting lines from a sand casting. Cold Box: Air set cores from a resin binder system in a core box. Cope: Top of a parted mold. Core: Molded sand component that creates the cavity in a casting that the pattern cannot form. Core Box: Tool used to create cores, usually wood, metal, or plastic.
    [Show full text]
  • Section 02 Tooling for Die Casting
    Tooling for Die Casting SECTION Section Contents NADCA No. Format Page Frequently Asked Questions (FAQ) 2-2 2 1 Introduction 2-3 2 Types of Die Casting Dies 2-4 2.1 Prototyping 2-4 2 2.2 Rapid Tooling Dies 2-4 2.3 Production Dies 2-5 2.4 Unit Dies 2-6 2.5 Trim Dies 2-6 3 Casting Features and Die Considerations 2-7 3.1 Core Slide Requirements 2-8 3.2 Parting Line: Cover & Ejector Die Halves 2-8 3.3 Ejector Pins 2-9 3.4 Cast-in Inserts 2-9 4 Die Materials 2-10 4.1 Die and Cavity Materials 2-10 4.2 Die Cavity Insert Materials 2-10 4.3 Die Steel Heat Treatment 2-11 5 Controlling Die Performance 2 -11 5.1 Porosity Control: Gating, Venting, Vacuum 2-11 5.2 Thermal Balancing 2-12 5.3 Oil Heating Lines 2-12 5.4 Alternate Surface Textures 2-12 5.5 Extended Die Life 2-12 6 Secondary Machining Preplanning 2-14 7 Gaging Considerations 2-14 8 Inherited Tooling 2-15 9 Engineering Consultation 2-15 10 Database Guidelines 2-16 11 New Die/Inherited Die Specifications 2-16 12 Die Life 2-16 13 Checklist for Die Casting Die Specifications T-2-1-12 Checklist 2-17 14 Guidelines to Increase Die Life T-2-2-12 Guideline 2-19 NADCA Product Specification Standards for Die Castings / 2015 2-1 Tooling for Die Casting A-PARTING LINE Surface where two die halves Frequently Asked Questions (FAQ) come together.
    [Show full text]