preprint(June 28, 2021) Time-reversal symmetry-breaking charge order in a correlated kagome superconductor C. Mielke III,1, 2, ∗ D. Das,1, ∗ J.-X. Yin,3, ∗ H. Liu,4, 5, ∗ R. Gupta,1 C.N. Wang,1 Y.-X. Jiang,3 M. Medarde,6 X. Wu,7 H.C. Lei,8 J.J. Chang,2 P. Dai,9 Q. Si,9 H. Miao,10 R. Thomale,11, 12 T. Neupert,2 Y. Shi,4, 5, 13 R. Khasanov,1 M.Z. Hasan,3, 14, 15, 16, y H. Luetkens,1 and Z. Guguchia1, z 1Laboratory for Muon Spin Spectroscopy, Paul Scherrer Institute, CH-5232 Villigen PSI, Switzerland 2Physik-Institut, Universit¨atZ¨urich,Winterthurerstrasse 190, CH-8057 Z¨urich,Switzerland 3Laboratory for Topological Quantum Matter and Advanced Spectroscopy (B7), Department of Physics, Princeton University, Princeton, New Jersey 08544, USA 4Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China 5School of Physical Sciences, University of Chinese Academy of Sciences, Beijing 100190, China 6Laboratory for Multiscale Materials Experiments, Paul Scherrer Institut, CH-5232 Villigen PSI, Switzerland 7Max-Planck-Institut fur Festkorperforschung, Heisenbergstrasse 1, D-70569 Stuttgart, Germany 8Department of Physics and Beijing Key Laboratory of Opto-electronic Functional Materials and Micro-nano Devices, Renmin University of China, Beijing 100872, China 9Department of Physics and Astronomy, Rice University, Houston, Texas 77005, USA 10Material Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, USA 11Institut fur Theoretische Physik und Astrophysik, Universitat Wurzburg, 97074 Wurzburg, Germany 12Department of Physics, Indian Institute of Technology Madras, Chennai 600036, India 13Songshan Lake Materials Laboratory, Dongguan, Guangdong 523808, China 14Princeton Institute for the Science and Technology of Materials, Princeton University, Princeton, New Jersey 08540, USA 15Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720, USA 16Quantum Science Center, Oak Ridge, Tennessee 37831, USA The kagome lattice, which is composed of a net- der intertwining with unconventional supercon- work of corner-sharing triangles, is a structural ductivity in the correlated kagome lattice. motif in quantum physics first recognized more 1 The observation of orbital currents is a long stand- than seventy years ago . It has been gradually ing motive in both topological and correlated quan- realized that materials which host such special tum matter. They have been suggested to produce lattice structures can exhibit quantum diversity, the quantum anomalous Hall effect when interacting ranging from spin-liquid phases, topological mat- 25 2{13 with Dirac fermions in a honeycomb lattice (Fig. 1a) ter to intertwined orders . Recently, charge and as the hidden phase of high-temperature cuprate sensitive probes have suggested that the kagome 26,27 14{16 superconductors (Fig. 1b). In both cases, orbital superconductors AV3Sb5 (A = K, Rb, Cs) 17{24 currents run through the lattice and break time-reversal exhibit unconventional chiral charge order , symmetry. Recently, the tantalizing visualization of which is analogous to the long-sought-after quan- such exotic order has been reported17{19 in the kagome tum order in the Haldane model25 or Varma 26 superconductor AV3Sb5 (A = K, Rb, Cs) (Fig. 1c). model . However, direct evidence for the time- Scanning tunneling microscopy observes a chiral 2×2 reversal symmetry-breaking of the charge order charge order (Fig. 1d) with an unusual magnetic field re- remains elusive. Here we utilize state-of-the-art sponse. Theoretical analysis17{24 also suggests that this muon spin relaxation to probe the kagome charge chiral charge order can not only lead to a giant anoma- order and superconductivity in KV3Sb5. We ob- lous Hall effect28 but also be a precursor of unconven- serve a striking enhancement of the internal field tional superconductivity23,29. However, the broken time- width sensed by the muon ensemble, which takes reversal symmetry nature of the charge order and its in- place just below the charge ordering temperature terplay with superconductivity has not been explicitly arXiv:2106.13443v1 [cond-mat.mtrl-sci] 25 Jun 2021 and persists into the superconducting state. Re- demonstrated by experiments. markably, the muon spin relaxation rate below the charge ordering temperature is substantially To explore unconventional aspects of supercon- enhanced by applying an external magnetic field. ductivity and the possible time-reversal symmetry We further show the multigap nature of super- breaking nature of charge order and superconductivity −2 in KV Sb , it is critical to measure the superconducting conductivity in KV3Sb5 and that the Tc/λab ratio 3 5 is comparable to those of unconventional high- order parameter and weak internal fields of KV3Sb5 temperature superconductors. Our results point on the microscopic level. Thus, we concentrate on to time-reversal symmetry breaking charge or- muon spin relaxation/rotation (µSR) experiments30,31 of the normal state depolarization rate and the magnetic 2 a Haldane Model b Varma Model c Orbital currents d in graphene in cuprates in kagome lattice Cu O 1nm Low High e Electronic clock f Positron detectors 3 �+ 1 Muon spin 2 Sample Muon detector 4 g h i Figure 1: Indication of time-reversal symmetry-breaking of the charge order in KV3Sb5. a; Orbital currents (red arrows) proposed in a honeycomb lattice. b; Orbital currents (red arrows) proposed in the CuO2 lattice of cuprates. c; Schematic of the orbital currents (red arrows) in the kagome lattice. d; Scanning tunneling microscopy of the Sb surface showing 2×2 charge order as illustrated by black lines. The inset is the Fourier transform of this image, shown lattice Bragg peaks marked by blue circles and 2×2 vector peaks marked by red circles. The three pairs of 2×2 vector peaks feature different intensities, denoting a chirality of the charge order. e; A schematic overview of the experimental setup. Spin polarized muons ◦ with spin Sµ, forming 60 with respect to the c-axis of the crystal, are implanted in the sample. The sample was surrounded by four detectors: Forward (1), Backward (2), Up (3), and Down (4). An electronic clock is started at the time the muon passes the muon detector and is stopped as soon as the decay positron is detected in the positron detectors. f; The ZF µSR time spectra for KV3Sb5, obtained at different temperatures, all above the superconducting transition temperature Tc. The solid black curves in panel a represent fits to the recorded time spectra, using the Eq. 1. g; The temperature dependences of the relaxation rates ∆ and Γ, obtained in a wide temperature range. h; The temperature dependence of Γ from two sets of detectors across the charge ordering temperature T ∗ ' 80 K. i; Temperature dependences of the muon spin relaxation rates ∆ and Γ, which can be related to the nuclear and electronic system respectively, in the temperature range across Tc. penetration depth λ in KV3Sb5. Importantly, zero-field netic fields as small as 0.1 G without applying external µSR (ZF-µSR) has the ability to detect internal mag- magnetic fields, making it a highly valuable tool for 3 probing spontaneous magnetic fields due to time-reversal We note that a similar value of internal magnetic field symmetry breaking32{36 within the superconducting strength is reported in several time-reversal symmetry- and charge ordered states. Additionally, λ is one of breaking superconductors32{34,36. Increase of the inter- the fundamental parameters of a superconductor, since nal field width visible from the electronic contribution to 2 it is related to the superfluid density ns via 1/λ = the ZF-µSR relaxation rate corresponds to an anomaly 2 ∗ ∗ µ0e ns=m (where m is the effective mass). seen also in the nuclear contribution to the relaxation rate ∆12; namely, a peak coinciding with the onset of While long-range magnetism has not been reported in the charge order, which decreases to a broad minimum 37 KV3Sb5 , zero-field µSR experiments have been carried before increasing again towards lower temperatures. out above and below T to search for any weak magnetism c In order to substantiate the above zero-field µSR re- (static or slowly fluctuating). A schematic overview of sults, systematic high field µSR39 experiments were car- the experimental setup with the muon spin forming 60◦ ried out (Fig. 2a). A non-monotonous behavior of the with respect to the c-axis of the crystal is shown in the relaxation rate is clearly seen in the µSR data, measured inset of Figure 1e. The sample was surrounded by four in magnetic field of 1 T, applied parallel to the c-axis, as detectors: Forward (1), Backward (2), Up (3), and Down (4). Figure 1f displays the zero-field µSR spectra from shown in Fig. 2b. We note that in high magnetic fields detectors 3 & 4 collected over a wide temperature range. we cannot discriminate between the nuclear and the elec- We see that the muon spin relaxation shows a reason- tronic contribution to the relaxation rate. Since the data able temperature dependence. Since the zero-field relax- at 1 T looks similar to the temperature dependence of ation is decoupled by the application of a small external the zero-field nuclear rate ∆12, it seems to be dominated magnetic field applied longitudinal to the muon spin po- by the nuclear response. However, at higher fields such as 3 T, 5 T and 8 T, the rate not only shows a broad larization, BLF = 50 G (see Fig. 1f), the relaxation is ∗ therefore due to spontaneous fields which are static on bump around T , but also shows a clear and stronger the microsecond timescale. The zero-field µSR spectra increase towards low temperatures within the charge or- were fitted using the gaussian Kubo-Toyabe depolariza- dered state, similar to the behavior observed for the re- tion function38, which reflects the field distribution at laxation rates Γ12 and Γ34 in zero-field.