SR 6/15/82 XR 4933591019 United StatesPatent [191 [11] 4,335,109 Hill [45] Jun. 15, 1982 [54] WATER REPELLENT AQUEOUS WOOD [5 6] References Cited TREATING SOLUTIONS U.S. PATENT DOCUMENTS Inventor: Robert E. Hill, Webster Groves, Mo. 2,571,030 10/1951 Govett et a1. ..................... 424/68 [75] 2,876,163 3/1959 Garizio et al. .................. .. 424/68 [73] Assignee: Koppers Company, Inc., Pittsburgh, Primary Examiner—-Lorenzo B. Hayes Pa. Attorney, Agent, or Firm-Donald M. MacKay [57] ABSTRACT [21] Appl. No.: 216,123 An increased water repellency is imparted to wood and [22] Filed: Dec. 15, 1930 other cellulosic materials with an aqueous solution con taining a mixture of an aluminum ~halohydrate and a water soluble salt of a mono, di or trivalent cation se Related US. Application Data lected from zinc, manganese, barium, calcium, cobalt, [63] Continuation of Ser. No. 96,333, Nov. 21, 1979, aban magnesium, nickel, copper, cadmium, strontium, beryl doned. lium, lead, mercury, chromium, sodium, lithium, and potassium and- a monovalent anion selected from for [51] 1m. (:1.3 .................... .. A01N 59/20;A01N 59/06 mate acetate, haloacetate, acrylate, methacrylate, propi [52] us. (:1. ..; ................................... .. 424/140; 106/2; onate, chloro and bromo-propionate, butyrate, isobu 106/1505; 424/145; 424/146; 424/150; tyrate, nitrate, sulfamate, iodide, bromide, and chloride, 424/153; 424/154; 424/289; 424/291; 424/293; said water soluble salt excluding the nitrates, sulfamates, I 424/294; 424/295; 427/440 chlorides and bromides of sodium, potassium and lith Field Of Search I. ............... .. 106/2, 1505; 424/68,. lum. 1 .~_.1424/140,_ 145,146, 150, 153, 154, 289, 291, ~ 293—295; 427/440 2 Claims, N0 Drawings 4,335,109 1 2 DETAILED DESCRIPTION OF THE WATER REPELLENT AQUEOUS WOOD INVENTION TREATING SOLUTIONS The non-aluminum metal salts can be prepared by This is a continuation of application Ser. No. 096,333, reacting a mono, di, or trivalent oxide with the appro ?led Nov. 21, 1979, now abandoned. priate acid. Thus, zinc propionate is made by reacting zinc oxide with propionic acid. SUMMARY OF THE INVENTION The aluminum halohydrates useful in the invention This invention relates to solutions that provide in can be represented by the formula: Alx(OH)yXZ, creased water repellency for wood and other cellulosic wherein X is a halogen such as chlorine, bromine, or iodine and x and y are integers of from 1 to 4 and z is an materials. More particularly, the invention is related to integer of from 5 to 1. The aluminum halohydrates are aqueous substantially sulfate free cellulosic materials usually polymeric in nature and thus the above formula treating solutions to include suspensions, comprising a should not be considered restrictive. Typical non-limit mixture of an aluminum halohydrate and a water solu ing examples of the aluminum halohydrates that can be ble salt of a mono, di or trivalent cation selected from used in the present invention are: Al3OH5Cl4, Al zinc, manganese, barium, calcium, cobalt, magnesium, 4OH10Cl2, Al4OH9Cl3, and Al2OI-I4Cl2. Inasmuch as nickel, copper, cadmium, ‘strontium, beryllium, lead, sulfate ion will precipitate the aluminum halohydrate, mercury, chromium, sodium, lithium, and potassium, the solution should be substantially free of sulfate. and a monovalent anion» selected from formate, acetate, 20 Any method of treating wood with aqueous treating haloacetate, acrylate, methacrylate, propionate, chloro solutions can be used when wood is treated with the and bromopropionate, butyrate, isobutyrate, nitrate, aqueous wood-treating solutions of the present inven sulfamate, iodide, bromide, and chloride, said water tion. These methods include treating wood by injection soluble salt excluding the nitrates, sulfamates, chlorides, of the aqueous wood-treating solution under pressure in and bromides of sodium, potassium, and lithium. The 25 closed vessels or dipping in open vessels or by brush or halo and halosubstituted anions can be chloro, bromo, spray painting of the solution. Also, in the method of or iodo. The solution can be used to treat paper, card treating wood with the aqueous wood treating solution board, and cellulosic materials generally, but for conve of the present invention, the wood may be end-sealed in nience, the disclosure describes the treatment of wood. any manner known to those skilled in the art to enhance Aluminum halohydrates which can be employed 30 the water repellent effect of the aqueous wood-treating include aluminum chlorohydrate, aluminum iodohy solution. In accordance with the invention, combination fungi drate, and aluminum bromohydrate. cide and water repellent solutions can be made by se Exemplary of suitable water soluble salts are: lecting a fungicide as the water soluble salt. Fungicides Zinc Acetate.2H2O 35 suitable for use as the water soluble salt can_be formed Zinc Propionate from one of the aforesaid anions and a cation selected Manganese (+2) AcetateAHgO from copper, zinc, barium, lithium, sodium, lead, mer Barium Acetate cury, cadmium, calcium, and potassium. Typical fungi Calcium Acetate cides which can be employed as the water soluble salt Calcium Iodoacetale include: cadmium formate, cadmium acetate, cadmium Calcium 2-Chloropropionate propionate, cadmium isobutyrate, cadmium butyrate, Calcium 3-Chloropropionate cadmium acrylate, cadmium nitrate, cadmium sulfa Calcium ,Isobutyrate mate, cadmium chloride, cadmium bromide, cadmium Calcium Acrylate iodide, cadmium iodacetate, cadmium chloroacetate, Lithium Acetate.2H2O 45 cadmium 2-chloropropionate, cadmium 3-chloropro Calcium Butyrate pionate, cupric formate, cupric acetate, cupric propio Calcium Propionate nate, cupric isobutyrate, cupric butyrate, cupric acry Calcium Formate late, cupric nitrate, cupric sulfamate, cupric chloride, Cobaltous (+2) Acetate.4H2O cupric bromide, cupric iodide, barium formate, barium acetate, barium propionate, barium isobutyrate, barium Magnesium Acetate.4H2O butyrate, barium acrylate, barium nitrate, barium sulfa Nickel (+ 2) Acetate.4H2O mate, barium chloride, barium bromide, barium iodide, Cupric Acetate.H2O barium iodoacetate, barium chloroacetate, barium 2 Lead ( + 2) Acetate.3H2O chloropropionate, barium 3-chloropropionate, zinc for Mercuric (+2) Nitrate, and -55 mate, zinc acetate, zinc propionate, zinc isobutyrate, Sodium Acetate.3H2O zinc butyrate, zinc acrylate, zinc nitrate, zinc sulfamate, Suitable but somewhat less effective than the preceding zinc chloride, zinc bromide, zinc iodide, zinc iodoace are: > tate, zinc chloroacetate, zinc 2-chloropropionate, zinc Zinc Nitrate.6H2O ' 3-chloropropionate, lithium formate, lithium acetate, Magnesium Nitrate.6H2O 60 lithium propionate, lithium isobutyrate, lithium buty Chromic (+ 3) AcetateJ-IZO rate, lithium acrylate, lithium iodide, lithium iodoace Cupric Nitrate.3I-I2O tate, lithium chloroacetate, lithium 2-chloropropionate, Zinc Chloride lithium 3-chloropropionate, sodium formate, sodium Zinc Sulfamate acetate, sodium propionate, sodium isobutyrate, ‘sodium Calcium Chloroacetate 65 butyrate, sodium acrylate, sodium iodide, sodium iod Cadmium Bromide.4H2O oacetate, sodium chloroacetate, sodium Z-chloropro Calcium Chloride.2H2O and pionate, sodium 3-chloropropionate, potassium formate, Potassium Iodide potassium acetate, potassium propionate, potassium 4,335,109 3 4 isobutyrate, potassium butyrate, potassium acrylate, The above solutions were diluted with water to one potassium iodide, potassium iodoacetate. potassium percent zinc metal content and tested for inhibition of chloroacetate, potassium 2'chloropropionate, potassium ceratocystis pillferi'a (a common sapstain fungus) mixed 3-chloropropionate, calcium formate, calcium acetate, with mold growth and spores from wet infected pine calcium propionate, calcium isobutyrate, calcium buty sapwood. Small,‘ clear, dry southern pine sapwood rate, calcium acrylate, calcium iodide, calcium iodoace specimens were vacuum treated with an aqueous sus' tate, calcium chloroacetate, calcium 2-chloropropion pension of the mold and sapstain spores to a very high ate, calcium 3-chloropropionate, mercury +2 acetate moisture content and dipped into the above described or nitrate with aluminum chlorohydrates and lead ace dilutions. After one week at room temperature and 100 tate. percent relative humidity, the untreated controls were Although the amount of aluminum halohydrate and heavily sapstained but none of the treated specimens water soluble salt employed will depend upon the par were attacked. The incubation period was continued for ticular materials employed, a treating solution will gen a total of three weeks with no sapstain attack on the erally contain from about 0.05 to about 2.0% aluminum treated specimens. The test was repeated using the first halohydrate and from about 0.06 to about 4.0% water two solutions diluted to a 0.06 percent zinc metal con soluble salt. A concentrate will generally contain either tent and there was no evidence of sapstain growth after powder or a solution of the more water soluble salts in 37 days. A solution of zinc acetate, 2H2O alone at an amount of from about 5 to 36% aluminum halohy 0.21% had no fungicidal effect against sapstain. drate and about 10% to 18% water soluble salt. Freshly planed dry southern pine sapwood boards The following description is directed to several alter 20 containing over 50% springwood on the area to be native embodiments of the aqueous wood-treating solu tested were treated with test solutions by