© 2000 ASM International. All Rights Reserved. www.asminternational.org Woldman’s Engineering Alloys, 9th Ed. (#06821G) ALLOY DATA / 17 A 1050 A 400* A 5557 A L 800* Comalco Ltd. Bergische Stahl Industrie Comalco Ltd. AL Tech Specialty Steel Corp. Commercially pure aluminum; Al 99.50 min. Stainless steel; C 0.08 max; Cr 13-15; Mn 1 Aluminum magnesium alloy; Cu 0.1; Mg Nickel iron superalloy; Al 0.6 max; C 0.1; Cr H12-temper: 97 MPa TS; 83 MPa YS; 15 El. max; Si 1 max. 0.6; Mn 0.2; bal Al. 19; Ni 30; Ti 0.6 max; bal Fe. H18-temper: 145 MPa TS; 138 MPa YS; 6 Ferritic type stainless steel. WNr. 1.4001. O-temper: 110 MPa TS; 41 MPa YS; 25 El. Resistant to oxidation and carburization at El. Chemical and process plant and H25-temper: 159 MPa TS; 138 MPa YS; 12 elevated temperatures. equipment. A 4543 El. Automobile trim. Comalco Ltd. A L 825* A 1100 Aluminum silicon alloy; Mg 0.3; Si 6; bal A 60 PB AL Tech Specialty Steel Corp. Comalco Ltd. Al. Westig (U.K.) Ltd. Nickel iron superalloy; C 0.05 max; Cr 19.5; Aluminum copper alloy; Al 99.0 min; Cu T1-temper: 145 MPa TS; 83 MPa YS; 20 El; Free machining steel; C 0.7; Mn 0.65; P Mo 3.5 max; Ni 38; bal Fe. 0.12. 40 Vickers. T8-temper: 207 MPa TS; 179 0.035 max; Pb 0.2; S 0.2; Si 0.2; bal Fe. Excellent corrosion resistance. O-temper: 90 MPa TS; 34 MPa YS; 35 El. MPa YS; 12 El; 75 Vickers. Architectural Free cutting steel. H18-temper: 165 MPa TS; 152 MPa YS; 5 extrusions. A M 3 DIE STEEL* El; 44 HB; Spinnings, holloware and general A 600* Balfour Darwins Ltd. sheet metal work. A 5* Bergische Stahl Industrie Cold work tool steel; C 0.4; Cr 5; Mo 1.35; Johnson Matthey plc, Materials Technology Cold work tool steel; C 1-1.1; Cr 0.9-1.1; Mn Si 1.05; V 1.1; bal Fe. A 1145 Division Europe 0.8-1.1; Si 0.15-0.3; W 1-1.3; bal Fe. For die casting dies, extrusion dies, upsetters; Comalco Ltd. See MATTHEY A 5. Cold work tool steel. WNr. 1.2419. air hardened, resists heat checking. Commercially pure aluminum; Al 99.45 min. General foil uses. A 500 H* A 6061 A METAL Bergische Stahl Industrie Comalco Ltd. Manufacturer unknown A 1199 Cold work tool steel; C 0.75-0.85; Co 0.9- Aluminum magnesium alloy; Cr 0.2; Cu Nickel steel; Cu 5-7; Ni 44; bal Fe. Comalco Ltd. 1.3; Cr 12.5-14.5; Mn 0.2-0.5; Si 0.3-0.6; bal 0.25; Mg 1; Si 0.6; bal Al. For sound transmitting devices. Commercially pure aluminum; Al 99.99 min. Fe. O-temper: 124 MPa TS; 55 MPa YS; 25 El; Electrical and electronic foil uses. Cold work tool steel. WNr. 1.2883. 30 HB; T6-temper: 310 MPa TS; 276 MPa A NICKEL ELECTRON GRADE* YS; 12 El; 95 HB; Structural applications, Criterion Metals, Inc. A 2011 A 5005 transport. See NICKEL 205. Comalco Ltd. Comalco Ltd. Aluminum copper alloy; Bi 0.5; Cu 5.5; Pb Aluminum magnesium alloy; Mg 0.8; bal Al. A 6262 A NICKEL* 0.5; bal Al. O-temper: 124 MPa TS; 41 MPa YS; 25 El. Comalco Ltd. Harrison Alloys Inc. T3-temper: 379 MPa TS; 296 MPa YS; 15 H18-temper: 200 MPa TS; 193 MPa YS; 4 Aluminum magnesium alloy; Bi 0.6; Cr 0.1; See HAI-NI 200. El: 110 Vickers. T4-temper: 310 MPa TS; El; 56 Vickers. H38-temper: 200 MPa TS; Cu 0.25; Mg 1; Pb 0.6; Si 0.6; bal Al. 145 MPa YS; 20 El. Screw machine products 186 MPa YS; 5 El; 51 HB; Appliances and T6-temper: 310 MPa TS; 276 MPa YS; 12 A PHOSPHOR BRONZE not requiring decorative anodizing. utensils, high strength foil. El; 100 Vickers. T9-temper: 400 MPa TS; Criterion Metals, Inc. 379 MPa YS; 10 El; 125 Vickers. Screw Phosphor bronze; Cu 94.82; Fe 0.1 max; P A 2024 A 5052 machine products suitable for decorative 0.05; Pb 0.05 max; Sn 5; Zn 0.3 max. Comalco Ltd. Comalco Ltd. anodizing. Thin gauge sheet, various tempers: 46-100 Aluminum copper alloy; Cu 4.5; Mg 1.5; Mn Aluminum magnesium alloy; Cr 0.25; Mg ksi TS min; 19-98 ksi YS min. ASTM B- 0.6; bal Al. 2.5; bal Al. A 70* 103. O-temper: 166 MPa TS; 76 MPa YS; 20 El. O-temper: 193 MPa TS; 90 MPa YS; 25 El; Crucible Materials Corp. T42 temper: 469 MPa TS; 310 MPa YS; 20 47 HB; H38-temper: 290 MPa TS; 255 MPa See CRUCIBLE A 70. A QUALITY El; 120 HB; Aircraft sheeting. YS; 7 El; 77 HB; Sheet metal work, marine Steelmark-Eagle & Globe, ANI Corporation applications. A 8 Limited A 25* English manufacture Water hardening tool steel; C 0.73; Mn 0.2; Johnson Matthey plc, Materials Technology A 5056 Cast magnesium aluminum alloy; Al 7.5-9; Si 0.2; V 0.2; bal Fe. Division Europe Comalco Ltd. Mn 0.15-0.4; Zn 0.3-1; bal Mg. Carbon, water hardened for punches, scale See MATTHEY A 25. Aluminum magnesium alloy; Cr 0.1; Mg 5.2; Sand cast: 140 MPa TS; 85 MPa YS; 2 El; pivots. AS1239 W2A-7; AISI W2. Mn 0.1; bal Al. 55 HB; General purpose sand or chill A 300* O-temper: 290 MPa TS; 152 MPa YS; 35 El; casting. BS 2970 MAG 1. A-10 SPB Bergische Stahl Industrie 70 Vickers. H38-temper: 414 MPa TS; 345 AFORA (Aceros Afora S.A.) Martensitic stainless steel; C 0.4-0.5; Cr 12- MPa YS; 15 El; 100 HB; Cable sheathing, A 8 H.P Carbon steel; C 0.05-0.15; Mn 1-1.5; P 0.07 14; Mn 1 max; Si 1 max; bal Fe. rivets, zippers, screen wire. English manufacture max; Pb 0.15-0.3; S 0.3-0.4; Si 0.06 max; bal Martensitic stainless steel. WNr. 1.4034. Cast magnesium aluminum alloy; Al 7.5-9; Fe. A 5086 Mn 0.15-0.7; Zn 0.3-1; bal Mg. Normalized at 900 C (16 mm): 39-52 A 3003 Comalco Ltd. Sand cast: 140 MPa TS; 85 MPa YS; 2 El; kgf/mm**2 TS; 22 kgf/mm**2 min YS; 20 Comalco Ltd. Aluminum magnesium alloy; Cr 0.15; Mg 4; 55 HB; Higher purity sand or chill casting. min El. Cold drawn (<16 mm): 52-82 Aluminum manganese alloy; Cu 0.12; Mn Mn 0.5; bal Al. BS 2970 MAG 2. kgf/mm**2 TS; 42 kgf/mm**2 min YS; 7 1.2; bal Al. O-temper: 262 MPa TS; 117 MPa YS; 22 El; min El. Cold drawn (<40 mm): 47-77 O-temper: 110 MPa TS; 41 MPa YS; 30 El. 60 HB; H38-temper: 359 MPa TS; 303 MPa A ALLOY-1 kgf/mm**2 TS; 38 kgf/mm**2 min YS; 8 H18-temper: 200 MPa TS; 186 MPa YS; 4 YS; 7 El. Unfired pressure vessels, TV National Physical Laboratory min El. El; 55 HB; Chemical equipment, sheet metal towers. Aluminum zinc alloy; Al 77; Cu 3; Zn 20. work, rigid foil containers. Hot rolled: 60,000 TS; 41,000 YS; 21 El; 36 A-10S A 5252 RA. For light alloy wrought parts; non- AFORA (Aceros Afora S.A.) A 3004 Comalco Ltd. hardenable. Carbon steel; C 0.05-0.15; Mn 1-1.5; P 0.07 Comalco Ltd. Aluminum magnesium alloy; Mg 2.5; bal Al. max; S 0.3-0.4; Si 0.06 max; bal Fe. Aluminum manganese alloy; Mg 1; Mn 1.2; H24 temper: 221 MPa TS; 159 MPa YS; 12 A ALLOY-2 Normalized at 900 C (16 mm): 39-52 bal Al. El. H28 temper: 283 MPa TS; 241 MPa YS; National Physical Laboratory kgf/mm**2 TS; 22 kgf/mm**2 min YS; 20 O-temper: 179 MPa TS; 69 MPa YS; 20 El. 5 El; 75 HB; High strength automobile trim. Aluminum copper alloy; Cu 4.7; Fe 0.5; Mg min El. Cold drawn (<16 mm): 52-82 H38-temper: 283 MPa TS; 248 MPa YS; 5 1.34; Ni 1.85; Pb 1.5; bal Al. kgf/mm**2 TS; 42 kgf/mm**2 min YS; 7 El; 70 HB; Storage tanks, car bodies, seam A 5454 For light alloy wrought parts; age- min El. Cold drawn (<40 mm): 47-77 welded tubing. Comalco Ltd. hardenable. kgf/mm**2 TS; 38 kgf/mm**2 min YS; 8 Aluminum magnesium alloy; Cr 0.1; Mg 2.7; min El. A 3203 Mn 0.8; bal Al. A L 75 Comalco Ltd. O-temper: 248 MPa TS; 117 MPa YS; 22 El; Sterling International Technology Ltd. A-110* Aluminum manganese alloy; Mn 1.2; bal Al. 62 HB; H34-temper: 303 MPa TS; 241 MPa Aluminum alloy; Cr 4-6; Cu 2.8-3.8; Mn 0.3- Heppenstall Co. H12 Temper: 131 MPa TS; 117 MPa YS; 32 YS; 10 El; 81 HB; Welded structures, 0.6; bal Al. Water hardening tool steel; C 1.2; Mn 0.3; Si El.