Aut Aut Research Journal ISSN NO: 0005-0601 STUDY OF MECHANICAL PROPERTIES ON COPPER TUNGSTEN COMPOSITES FOR RESISTIVITY APPLICATIONS Dr. RAVINAIK BANOTH DUDDU RAVEENDRA Professor in Mechanical Engg dept, ASSISTANT Professor in Mechanical St martin's Engineering College, Engg dept, CMR Engineering College, Dhulapally Road Secundrabad-500100, Medchal Road Secundrabad-500100, E [email protected] mail id [email protected] ABSTRACT: Tungsten copper (W-Cu) composites, as a traditional refractory material, are promising materials for manufacture of electrical contacts and electrodes, heavy duty electronic contacts, welding and electro-forging dies, heat sinks, packaging material, arcing resistance electrodes and thermal management devices owing to their excellent properties. This critical review presents and discusses the current progress of W-Cu composites. Fabrication of net-shape tungsten–copper (W–Cu) composites has attracted more attention in recent years due to its good performance for wide applications, In this research, W–Cu composite including 20 wt.%, 25 wt.%, or 30 wt.% Cu. was produced by powder metallurgy technique using wet mixtures of elemental powders. Cold compaction was carried out under pressures from 300 to 1200 MPa, while sintering was achieved in vacuum at 1400 °C for 1 h, and 2 h. The particle size and shape of powders, as well as the microstructure after wet mixing, compaction, and sintering were investigated by using SEM. Keywords: Tungsten-copper composites, Preparation method, Modification, Application 1.0 Introduction Tungsten-copper (W-Cu) composites is a typical composite consisting of high strength tungsten (W) and low melting copper (Cu) phases, which are promising materials for manufacture of electric contact parts, heat sinks in high-power microelectronic devices, arcing-resistant electrodes, deviator plates for fusion reactors, anti-ultra-high temperature erosion nuzzles, etc. Their use in these applications is based on a combination of properties (as shown in Table 1), including the high hardness, erosion and electric-erosion resistance, the low coefficients of thermal expansion and wear resistance of W, and the outstanding electrical and thermal conductivity of Cu Furthermore, W-Cu composites exhibit better machinability compared with pure W. Powder Metallurgy (P/M), however, offers a reasonably good solution to W fabrication problems exploiting its near net-shaping capability Tungsten particle-reinforced copper composites: One promising class of W–Cu materials of interest with regard to PFC applications are Wp article-reinforced Cu (Wp–Cu) composites. Such materials can be produced by means of Cu melt infiltration of powder metallurgically produced open porous W skeletons. Following such an approach, the typically realisable material composition ranges from 60 wt.%W–40 wt.% Cu to 90 wt.%W–10 wt.% Cu which corresponds to approximately 40 vol. %W–60 vol.% Cu to 80 vol.% W–20 vol.% Cu. It has long been recognised that such composite metals offer an interesting combination of material properties Nowadays, Wp–Cu composites are for example used as contact materials in high voltage applications due to their high thermal and electrical conductivity, their high temperature stability, as well as their high ablation resistance 2.0 LITERATURE REVIEW: Hamidi AG, Arabi H, Rastegari [1] typical micrographs of a Wp–Cu composite with 60 wt.%W–40 wt.%Cu (W–40Cu) are shown. The two different phases can clearly be Volume XI, Issue VI, June/2020 Page No:129 Aut Aut Research Journal ISSN NO: 0005-0601 distinguished. Furthermore, it can be seen that the material is fully infiltrated with Cu and that it does not show any plainly visible porosity which is a prerequisite for acceptable thermophysical and mechanical properties of the material. Wang C, Lin YC [2] W–Cu composite materials are promising candidates regarding the application to the heat sink of highly loaded PFCs. The present contribution summarises recent results regarding the manufacturing and characterisation of such W–Cu composite materials produced by means of liquid Cu melt infiltration of open porous W preforms. On the one hand, this includes composites manufactured by infiltrating powder metallurgically produced W skeletons Jigui C, Lei W, Yanbo C [3] the electrical, mechanical and physical properties of Cu-WC composites are presented. The composites of copper alloy containing 0–8 weight % WC were prepared using liquid metallurgy route by stirring molten alloy to obtain vortex using a steel stirrer coated with alumina and rotated at 500 rpm. The experimental results showed that the density of the composites increase with increased WC content and agrees with the values obtained through the rule of mixtures. Hashempour M, Razavizadeh [4] Metal matrix composites (MMCs) are materials which consist of metal alloys reinforced with continuous fibers, whiskers or particulates. They are designed to combine the desirable attributes of metals and ceramics. Their properties are an intermediate between matrix alloy and ceramic reinforcement 3.0 MATERIALS AND METHODS Composite materials are mainly known for the simultaneous benefiting of different properties of non-identical materials. Metal matrix composites (MMC's) have gained great importance over the last two decades and their applications have increasingly become popular Due to a unique combination of the high electrical and thermal conductivities of copper, and the low coefficient of thermal expansion (CTE), high hardness, high melting point (3410 °C), low vapor pressure, and high arc erosion resistance of tungsten, these elements are very good candidates for production of composites having suitable thermoelectrical and arc resistance properties Tungsten–copper composites have a high corrosion and erosion resistances, and act as good conductors for both current and heat, and have low coefficient of thermal expansion (CTE). They also exhibit excellent mechanical properties and homogeneous microstructure. Hence, they are needed for high performance, and referred to as advanced engineering materials W–Cu composites have been widely used for thermal and electrical applications, as arc resistant electrodes, ultrahigh-voltage electric contact materials, microwave packages, heavy duty electrical contacts, in microelectronics devices, heat sink materials for high density integrated circuits, welding electrodes for electro discharge machining (EDM), and high ablation resistance Volume XI, Issue VI, June/2020 Page No:130 Aut Aut Research Journal ISSN NO: 0005-0601 Figure: the effect of processing parameters, such as mixing, compaction, and sintering, on the properties of W–Cu composites. Experimental work: Raw powders of W (99.95 wt.%, and 0.25–1 μm) and Cu (99.99 wt.%, and 10–60 μm), from Buffalo Tungsten Inc, and Sherwood Medical, respectively, were used as raw materials. Mixtures containing 20 wt.%, 25 wt.%, and 30 wt.% Cu were prepared by wet rod milling, Fig. 1. The wet rod milling was performed by using stainless steel cylindrical rods, at weight ratio of rods to powder of 10:1. The volume of the container to the volume of rods was 3:1. Mixing was carried out at 140 rpm for 6 h. Besides, the powders were mixed with 0.5 wt.% paraffin wax as a lubricant to reduce friction during compaction. Cold compaction of specimens with different compositions was then carried out at room temperature under various pressures; 300, 600, 900 and 1200 MPa. The green compacts were sintered in a vacuum furnace with graphite heating elements under vacuum (10−2 Torr), Fig. The samples were first heated at a rate of 3 °C/min up to 450 °C. To dry any moister content in through 120 °C, and expel any gases captured in the pores, the samples were kept at 450 °C for 30 min. The temperature was then raised to 850 °C for 30 min to facilitate solid phase sintering. Figure: Heating cycle for the vacuum sintering process Volume XI, Issue VI, June/2020 Page No:131 Aut Aut Research Journal ISSN NO: 0005-0601 Figure: SEM photographs of investigated powders. (a) Pure tungsten powder, (b) pure copper powder used in present study. liquid phase sintering process. In both cases, the temperature was raised again to 1400 °C. The first group was sintered for 1 h, while the second group was sintered for 2 h. Finally, the furnace was turned off and the sintered specimens were cooled over 8 h using a water-cooling system. To calculate the volume shrinkage of each specimen, 11 mm diameter and 7 mm thick green compacts, the dimensions of the cold compacts and those of the sintered specimens were measured using a dial gauge micro meter of 1 μm sensitivity. Then, the samples were polished with 3 μm diamond paste. The microstructure of the polished samples was investigated by optical microscopy and composites microstructure was studied by using scanning electron microscope (SEM). Volume XI, Issue VI, June/2020 Page No:132 Aut Aut Research Journal ISSN NO: 0005-0601 Figure: SEM photographs after wet mixing of investigated powders: (a) W-25wt.%Cu, (c) W-20wt.%Cu. W-30wt.%Cu, (b) W-25wt.%Cu, (c). W-20wt.%C. 4.0 Results and discussion SEM micrographs of pure W and pure Cu powders are shown in Fig. Tungsten particles have fine spherical structure with a size range of approximately 0.5–1 μm. Cu-powders have fine flake structure with a particle size between 10 and 60 μm. Fig. shows (SEM) photographs after wet mixing of investigated powders. The figure reveals relatively homogeneous distribution of both copper and tungsten powders. It is also observed that the fined spherical tungsten particles (0.5–1 μm) cover the relatively large copper flakes (10–60 μm). Moreover, the W–Cu mixtures where analysed using this energy dispersive X-ray spectroscopy (EDS), as shown in Fig. which existence confirms spectra of both W and Cu. Figure: EDS analysis of W–Cu mixtures, (a)W-30wt.%Cu, (b) W-25wt.%Cu, (c) W- 20wt.%Cu. rearrangement, decreasing pores, and increasing contact regions. The flake shape of copper powder may have facilitated the increase of density at higher pressure.