Dupont Zytel 330 Clear

Zytel® 330 NC010 Polyamide DuPont Engineering Polymers Product Description Zytel® 330 NC010 is a transparent polyamide resin with amorphous characteristics. General Manufacturer / Supplier • DuPont Engineering Polymers Generic Symbol • Nylon, Unspecified Material Status • Commercial: Active Availability • Europe • North America RoHS Compliance • Contact Manufacturer Appearance • Clear/Transparent Forms • Pellets Processing Method • Injection Molding Part Marking Code (ISO 11469) • >PA< Resin ID (ISO 1043) • PA

Physical Test Method Unit Dry Conditioned Specific Gravity ASTM D792 g/cm³ 1.18 -- ISO 1183 Molding Shrinkage Flow Internal Method % 0.50 -- Across Flow Internal Method % 0.50 -- Flow: 2.00 mm ISO 294-4 % 0.50 -- Water Absorption 24 hr, 23°C ASTM D570 % 0.45 -- Saturation, 23°C ASTM D570 % 5.8 -- ISO 62 Mechanical Test Method Unit Dry Conditioned Tensile Modulus 23°C ASTM D638 MPa 2360 -- 23°C ISO 527-2 MPa 2400 -- Tensile Stress Yield, 23°C ISO 527-2 MPa 97.0 90.0 23°C ASTM D638 MPa 97.0 90.0 Tensile Strain Yield, 23°C ISO 527-2 % 6.0 -- Break, 23°C ASTM D638 % 220 250 Flexural Modulus (23°C) ASTM D790 MPa 2800 3100 Impact Test Method Unit Dry Conditioned Charpy Notched Impact Strength ISO 179/1eA -40°C kJ/m² 4.5 -- 23°C kJ/m² 9.9 -- Charpy Unnotched Impact Strength ISO 179/1eU -40°C kJ/m² 230 -- 23°C kJ/m² 180 -- Notched Izod Impact 23°C ASTM D256 J/m 81.0 96.0 23°C ISO 180/1A kJ/m² 8.00 -- Unnotched Izod Impact (23°C) ASTM D4812 No Break No Break Hardness Test Method Unit Dry Conditioned Rockwell Hardness (R-Scale, 23°C) ASTM D785 128 --

The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. Zytel® 330 NC010 Wednesday, February 10, 2010 Polyamide DuPont Engineering Polymers Thermal Test Method Unit Dry Conditioned Deflection Temperature Under Load 0.45 MPa, Unannealed ASTM D648 °C 127 -- ISO 75-2/B 1.8 MPa, Unannealed ASTM D648 °C 123 -- ISO 75-2/A CLTE - Flow -- ASTM D696 cm/cm/°C 0.000061 -- 23 to 55°C ASTM E831 cm/cm/°C 0.000062 -- ISO 11359-2 Electrical Test Method Unit Dry Conditioned Volume Resistivity -- ASTM D257 ohm·cm 1.0E+15 1.0E+15 -- IEC 60093 ohm·cm 1.0E+15 -- Dielectric Strength 2 ASTM D149 23°C kV/mm 13 330 23°C, 3.20 mm kV/mm 13 13 Dielectric Constant 1 kHz ASTM D150 4.10 4.30 1 MHz ASTM D150 3.70 3.80 23°C, 1 MHz IEC 60250 3.70 3.80 Dissipation Factor 23°C, 1 kHz ASTM D150 0.020 0.020 23°C, 1 MHz ASTM D150 0.020 0.020 IEC 60250 Flammability Test Method Unit Dry Conditioned Flame Rating - UL UL 94 0.860 mm V-2 -- 1.60 mm V-2 -- 3.00 mm V-2 -- Flammability Classification IEC 60695-11-10, -20 0.860 mm V-2 -- 1.60 mm V-2 -- 3.00 mm V-2 -- UL 746 Test Method Unit Dry Conditioned RTI Str UL 746 0.860 mm °C 90.0 -- 1.50 mm °C 90.0 -- 3.00 mm °C 90.0 -- RTI Imp UL 746 0.860 mm °C 65.0 -- 1.50 mm °C 65.0 -- 3.00 mm °C 65.0 -- RTI Elec UL 746 0.860 mm °C 90.0 -- 1.50 mm °C 90.0 -- 3.00 mm °C 90.0 -- Comparative Tracking Index (CTI) UL 746 V 600 --

Injection Nominal Value Unit Drying Temperature 80.0 °C Drying Time 6.0 to 10 hr Suggested Max Moisture 0.10 % Processing (Melt) Temp 280 to 320 °C Mold Temperature 70.0 to 95.0 °C Melt Temperature, Optimum 300 °C Mold Temperature, Optimum 80 °C 2 of 3 Copyright © 2010 - IDES - The Plastics Web ® | 800-788-4668 or 307-742-9227 | www.ides.com. Document Created: Wednesday, February 10, 2010